PC DS-3002R MITSUBISHI ENGINEERING JAPAN
IUPILON™
Casters
Thermal stability,High crystallinity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/DS-3002R |
---|---|---|---|
Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/DS-3002R |
---|---|---|---|
Tensile modulus | ISO 527-2 | 2500 Mpa | |
Nominal tensile fracture strain | ISO 527-2 | 100 % | |
bending strength | ISO 178 | 89.0 Mpa | |
Flexural modulus | ISO 178 | 2300 Mpa | |
Tensile strain | 屈服 | ISO 527-2 | 6.5 % |
tensile strength | 屈服 | ISO 527-2 | 59.0 Mpa |
Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/DS-3002R |
---|---|---|---|
Volume resistivity | IEC 60093 | 3E+16 ohms·cm | |
Surface Resistivity | IEC 60093 | 6E+15 ohms | |
Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/DS-3002R |
---|---|---|---|
UL flame retardant rating | 0.40mm | UL 94 | V-2 |
physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/DS-3002R |
---|---|---|---|
Shrinkage rate | TD:3.20mm | 0.50-0.70 % | |
Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 14.0 cm3/10min |
Shrinkage rate | 吸水率(饱和,23°C) | 0.24 % | |
MD:3.20mm | 0.50-0.70 % | ||
melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 14 g/10min |
Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/DS-3002R |
---|---|---|---|
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 134 °C |
1.8MPa,未退火,HDT | ISO 75-2/A | 121 °C | |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.5E-05 cm/cm/°C |
TD | ISO 11359-2 | 6.6E-05 cm/cm/°C |