Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LZ2510V IDEMITSU JAPAN
TARFLON™
LCD application,light-emitting diode
Flame retardant,UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | IDEMITSU JAPAN/LZ2510V |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 120 |
| M计秤 | ISO 2039-2 | 50 |
| Supplementary Information | Test Condition | Test Method | IDEMITSU JAPAN/LZ2510V |
|---|---|---|---|
| ISO Shortcut | >PC< |
| Electrical performance | Test Condition | Test Method | IDEMITSU JAPAN/LZ2510V |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/LZ2510V |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2 | 80 % | |
| bending strength | ISO 178 | 100 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 40 kJ/m² | |
| Flexural modulus | ISO 178 | 2300 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 60 Mpa |
| elongation at break | ISO 527-2 | 80 % |
| flammability | Test Condition | Test Method | IDEMITSU JAPAN/LZ2510V |
|---|---|---|---|
| UL flame retardant rating | 0.9mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | IDEMITSU JAPAN/LZ2510V |
|---|---|---|---|
| Melt volume flow rate | MVR | ISO 1133 | 3 cm3/10min |
| Shrinkage rate | TD:2.00mm | 内部方法 | 0.50-0.70 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 4.00 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.23 % |
| Shrinkage rate | MD: 2.00 mm | 内部方法 | 0.5-0.7 % |
| TD | 内部方法 | 0.5-0.7 % | |
| MD:2.00mm | 内部方法 | 0.50-0.70 % | |
| Water absorption rate | 平衡,23℃, 50% RH | ISO 62 | 0.23 % |
| Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/LZ2510V |
|---|---|---|---|
| Linear coefficient of thermal expansion | ISO 11359-2 | 0.000065 cm/cm/℃ | |
| UL flame retardant rating | 1.00 mm | UL 94 | V-0 |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 129 °C |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 129 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI Str | UL 746 | 80.0 °C | |
| RTI Elec | UL 746 | 80.0 °C |