| Impact resistance | Test Condition | Test Method | 4Plas/9K22140 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 kJ/m² |
| 23°C | ISO 180/1A | 9.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | 4Plas/9K22140 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 1.5 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 150 MPa |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 9.0 kJ/m² |
| Tensile modulus | 23°C | ISO 527-2/5 | 11000 MPa |
| Tensile strain | 断裂, 23°C | ISO 527-2/5 | 1.5 % |
| tensile strength | 断裂, 23°C | ISO 527-2/5 | 150 MPa |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 kJ/m² |
| Heat distortion temperature | Test Condition | Test Method | 4Plas/9K22140 |
|---|---|---|---|
| flammability | UL 阻燃等级，1.60 mm | UL 94 | HB |
| 热灯丝点火温度，2.00 mm | IEC 60695-2-13 | 650 °C |
| flammability | Test Condition | Test Method | 4Plas/9K22140 |
|---|---|---|---|
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 650 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | 4Plas/9K22140 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.10 % |
| 平衡,23°C,50%RH | ISO 62 | 0.10 % | |
| density | ISO 1183 | 1.65 g/cm³ |
| Thermal performance | Test Condition | Test Method | 4Plas/9K22140 |
|---|---|---|---|
| Heat distortion temperature | 维卡软化温度，HDT | ISO 306/B | 215 °C |
| vicat | ISO 306/B | 215 °C | |
| melting temperature | ISO 11357 | 225 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 215 °C |
| 熔融温度，HDT | ISO 11357 | 225 °C | |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 215 °C |