PMMA TF8 MITUBISHI RAYON JAPAN

ACRYPET™

Automotive components,Casters,Light guide plates for laptops

Flame retardant,High temperature resistan,UV resistance,Suitable for small sizes,Thin light guide plate

Plastic Datasheets

Basic Performance	Test Condition	Test Method	MITUBISHI RAYON JAPAN/TF8
Water absorption rate	24hr	ISO 62	0.3 %

thermal performance	Test Condition	Test Method	MITUBISHI RAYON JAPAN/TF8
Heat transfer rate		JIS A1412	0.2 W/(m?℃)
Hot deformation temperature	1.80MPa	ISO 75-2	95 °C
Linear coefficient of thermal expansion		JIS K7197	6×10 1/℃
melt mass-flow rate	230℃,37.3N	ISO 1133	10 g/10min
specific heat		JIS K7123	1.5 J/(g?℃)
Spiral flow length	厚薄2mm,230℃	三菱丽阳法	220 mm
Spiral flow length		厚薄2mm,250℃	三菱丽阳法	340 mm
Vicat softening temperature	50N	ISO 306	102 °C

mechanical properties	Test Condition	Test Method	MITUBISHI RAYON JAPAN/TF8
Bending modulus		ISO 178	3.3 GPa
bending strength		ISO 178	90 Mpa
elongation	1A/5	ISO 527-2	5 %
Impact strength of cantilever beam gap	1eU 无槽口	JIS K7111	21 KJ/m
		1A	JIS K7110	1.6 KJ/m
		1eA V槽口	JIS K7111	1.2 KJ/m
Rockwell hardness		ISO 2039	101 M Scale
Tensile modulus	1A/1	ISO 527-2	3.3 GPa
tensile strength	1A/5	ISO 527-2	59 Mpa

Electrical performance	Test Condition	Test Method	MITUBISHI RAYON JAPAN/TF8
Arc resistance		JIS K6911	没有痕迹
Dielectric constant	60Hz	JIS K6911	3.7
dielectric loss tangent	60Hz	JIS K6911	0.05
Dielectric strength	4kV/sec	JIS K6911	20 MV/m
Volume resistivity		JIS K6911	>10 Ωm
Volume resistivity			JIS K6911	>10 Ω

Physical properties	Test Condition	Test Method	MITUBISHI RAYON JAPAN/TF8
Refractive index	N	ISO 489	1.49
Transmittance rate	3mm	ISO 13468-1	93 %
turbidity	3mm	ISO 14782	0.3 %