PA6T C230NK MITSUI CHEM JAPAN
ARLEN™ 
Electrical field、Electronic field
Glass fiber reinforced、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Other performanceTest ConditionTest MethodMITSUI CHEM JAPAN/C230NK
Glass Fiber Content30 %
Basic performanceTest ConditionTest MethodMITSUI CHEM JAPAN/C230NK
Water absorption rate23℃,24小时在水里(2mmt,100℃)ASTM D-5700.3(3.0) %
Mechanical propertiesTest ConditionTest MethodMITSUI CHEM JAPAN/C230NK
elongationdry(moist)ASTM D-6383(3) %
Flexural modulusdry(moist)ASTM D-79012000(8500) Mpa
Rockwell hardnessASTM D-785110 M Scale
tensile strength dry(moist)ASTM D-638170(140) Mpa
Impact strength of cantilever beam gapdry(moist)ASTM D-25670(80) J/m
bending strengthdry(moist)ASTM D-790260(220) Mpa
Electrical performanceTest ConditionTest MethodMITSUI CHEM JAPAN/C230NK
dielectric strengthdryASTM D-14920 KV/mm
Dissipation Factor10ASTM D-1500.012
Volume resistivitydryASTM D-25710 Ω.cm
dielectric constant10ASTM D-1503.9
physical property Test ConditionTest MethodMITSUI CHEM JAPAN/C230NK
Shrinkage rate2mmtASTM D-9550.4(0.8) %
Thermal performanceTest ConditionTest MethodMITSUI CHEM JAPAN/C230NK
Heat distortion temperatureHDTASTM D-648295 °C
Linear coefficient of thermal expansionASTM D-6962.4(5.0)
melting temperature310 °C
Glass transition temperature (Tg)85 °C
UL flame retardant ratingUL 94V-0