PC Lupoy® GN1002FC LG Chem Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG Chem Ltd./Lupoy® GN1002FC |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 660 J/m |
| Mechanical properties | Test Condition | Test Method | LG Chem Ltd./Lupoy® GN1002FC |
|---|---|---|---|
| elongation | 断裂,3.20mm | ASTM D638 | >100 % |
| bending strength | 3.20mm | ASTM D790 | 93.2 MPa |
| Flexural modulus | 3.20mm | ASTM D790 | 2260 MPa |
| tensile strength | 屈服,3.20mm | ASTM D638 | 63.7 MPa |
| flammability | Test Condition | Test Method | LG Chem Ltd./Lupoy® GN1002FC |
|---|---|---|---|
| UL flame retardant rating | 2.0mm | UL 94 | V-0 |
| 1.5mm | IEC 60695-11-10,-20 | V-0 | |
| 1.5mm | UL 94 | V-0 | |
| 2.0mm | IEC 60695-11-10,-20 | V-0 |
| physical property | Test Condition | Test Method | LG Chem Ltd./Lupoy® GN1002FC |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.50to0.80 % |
| density | ASTM D792 | 1.20 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 17 g/10min |
| Thermal performance | Test Condition | Test Method | LG Chem Ltd./Lupoy® GN1002FC |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 117 °C |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI Str | UL 746 | 80.0 °C | |
| RTI Elec | UL 746 | 80.0 °C |