Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI EC-1006 BKNAT(EE006-BKNAT) SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Automotive components、Communication equipment
Flame retardant、Carbon fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/EC-1006 BKNAT(EE006-BKNAT) |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 26 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 2.47 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.2 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 7.80 J |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/EC-1006 BKNAT(EE006-BKNAT) |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1.0E+2to1.0E+6 ohms |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/EC-1006 BKNAT(EE006-BKNAT) |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 20900 Mpa | |
| bending strength | ASTM D790 | 280 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 197 Mpa |
| 断裂 | ISO 527-2 | 183 Mpa | |
| Wear factor | Washer | ASTM D3702Modified | 75.0 10^-10in^5-min/ft-lb-hr |
| Flexural modulus | ASTM D790 | 18200 Mpa | |
| Tensile modulus | ASTM D638 | 19400 Mpa | |
| elongation | 断裂 | ASTM D638 | 1.3 % |
| bending strength | ISO 178 | 269 Mpa | |
| coefficient of friction | Static | ASTM D3702Modified | 0.48 |
| Tensile strain | 断裂 | ISO 527-2 | 1.1 % |
| Flexural modulus | ISO 178 | 17900 Mpa | |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.52 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/EC-1006 BKNAT(EE006-BKNAT) |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.10 % |
| MD：24小时 | ASTM D955 | 0.10-0.30 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.20 % |
| 平衡,23°C,50%RH | ISO 62 | 0.29 % | |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.30-0.50 % |
| TD:24小时 | ISO 294-4 | 0.39 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/EC-1006 BKNAT(EE006-BKNAT) |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 2.2E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 2.3E-05 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 3.6E-05 cm/cm/°C | |
| MD：-40到40°C | ISO 11359-2 | 3.6E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 219 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 218 °C |