Product Name
Brand Name
Usages
Properties
Certificates

PC URZ2502 IDEMITSU JAPAN
TARFLON™
Automotive Applications,Home appliance components
High temperature resistan,Flame retardant,transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Other performance | Test Condition | Test Method | IDEMITSU JAPAN/URZ2502 |
---|---|---|---|
Light reflectance | D65 type,10 | 97.5 | |
Melt Volume Flow Rate (MVR) | ISO 1133 | 20 cm3/10min | |
Transmittance rate | 1mmt | 0.3 |
thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/URZ2502 |
---|---|---|---|
Combustibility (rate) | UL 94 | V-0/1.5mm | |
Hot deformation temperature | 0.46MPa | ISO 75-1-2 | 127 °C |
1.8MPa | ISO 75-1-2 | 117 °C | |
UL flame retardant rating | 1.5mm | UL 94 | V-0 |
mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/URZ2502 |
---|---|---|---|
Bending modulus | ISO 178 | 2600 Mpa | |
ASTM D790/ISO 178 | 2.6(GPa) kg/cm²(MPa)[Lb/in²] | ||
bending strength | ASTM D790/ISO 178 | 90 kg/cm²(MPa)[Lb/in²] | |
ISO 178 | 90 Mpa | ||
elongation | Break | ISO 527-1 | 80 % |
Elongation at Break | ASTM D638/ISO 527 | tB 80 % | |
Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 50 kg·cm/cm(J/M)ft·lb/in | |
ISO 176 | 50 k/Jm2 | ||
Tensile modulus | ISO 527-1 | 2400 Mpa | |
tensile strength | ASTM D638/ISO 527 | 60 kg/cm²(MPa)[Lb/in²] | |
Tensile stress | ISO 527-1 | 60 Mpa |
other | Test Condition | Test Method | IDEMITSU JAPAN/URZ2502 |
---|---|---|---|
characteristic | 高反射、遮光性、非臭素、阻燃 |
Physical properties | Test Condition | Test Method | IDEMITSU JAPAN/URZ2502 |
---|---|---|---|
density | ASTM D792/ISO 1183 | 1.33 | |
melt mass-flow rate | ASTM D1238/ISO 1133 | 21 cm3/10min(300℃/1.2kg ) g/10min |