Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 4701-7000 SABIC INNOVATIVE US
LEXAN™
Electronic and electrical
High temperature resistan、transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/4701-7000 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 46 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 13 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 11 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 35 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/4701-7000 |
|---|---|---|---|
| Rockwell hardness | R 计秤 | ISO 2039-2 | 127 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/4701-7000 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2300 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 70.0 Mpa |
| Flexural modulus | ISO 178 | 2300 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | > 50 % |
| 屈服 | ISO 527-2/50 | 7.0 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/4701-7000 |
|---|---|---|---|
| Dissipation Factor | 100 Hz | IEC 60250 | 0.026 |
| relative permittivity | 1 MHz | IEC 60250 | 3.10 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/4701-7000 |
|---|---|---|---|
| Burning wire flammability index | 2.0 mm | IEC 60695-2-12 | 850 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/4701-7000 |
|---|---|---|---|
| Melt volume flow rate | 300°C/5.0 kg | ISO 1133 | 6.00 cm3/10min |
| Shrinkage rate | Flow | 内部方法 | 0.90 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/4701-7000 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 170 °C |
| thermal conductivity | ISO 8302 | 0.21 W/m/K | |
| Heat distortion temperature | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距，HDT | ISO 75-2/Be | 165 °C |
| vicat | -- | ISO 306/A50 | 185 °C |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距，HDT | ISO 75-2/Ae | 150 °C |
| vicat | -- | ISO 306/B50 | 175 °C |
| ball-indentation hardness | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | 23 到 80°C，流动 | ISO 11359-2 | 8.0E-5 cm/cm/°C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/4701-7000 |
|---|---|---|---|
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 310 to 330 °C | ||
| Temperature at the rear of the barrel | 300 to 320 °C | ||
| Processing (melt) temperature | 325 to 360 °C | ||
| Hopper temperature | 60 to 80 °C | ||
| drying temperature | 125 to 135 °C | ||
| Temperature at the front of the material cylinder | 320 to 340 °C | ||
| Temperature | 100 to 125 °C | ||
| Spray nozzle temperature | 320 to 340 °C |
Contact Us
Get App