ABS IM15 ASAHI JAPAN
Stylac™
Home appliance components
--
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | ASAHI JAPAN/IM15 |
|---|---|---|---|
| Rockwell hardness | R计秤,2.50mm | 104 |
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/IM15 |
|---|---|---|---|
| melt mass-flow rate | JIS K7210 | 8 g/10min |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/IM15 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 49.7 Mpa |
| Impact strength of cantilever beam gap | -30℃ | ASTM D-256 | 108 J/m |
| bending strength | ISO 178 | 80.2 Mpa | |
| Flexural modulus | ISO 178 | 2500 Mpa | |
| ASTM D-790 | 2646 Mpa | ||
| bending strength | ASTM D-790 | 74 Mpa | |
| Impact strength of cantilever beam gap | 23℃ | ASTM D-256 | 333 J/m |
| Rockwell hardness | ASTM D-785 | 110 R-Scale | |
| tensile strength | ASTM D-638 | 46 Mpa | |
| Impact strength of cantilever beam gap | 0℃ | ASTM D-256 | 196 J/m |
| elongation at break | ASTM D-638 | 50 % |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/IM15 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.05 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 7.0 g/10min |
| flammability | Test Condition | Test Method | ASAHI JAPAN/IM15 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ASAHI JAPAN/IM15 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.40-0.60 % |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 7.60 cm3/10min |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 7.2 g/10min |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/IM15 |
|---|---|---|---|
| vicat | ISO 306/B | 105 °C | |
| Heat distortion temperature | HDT | ASTM D-648 | 90 °C |
| vicat | ASTM D-1525 | 113 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 84.0 °C |
| RTI Imp | UL 746 | 60.0 °C | |
| RTI | UL 746 | 60.0 °C | |
| ball-indentation hardness | EMAC | 95 °C | |
| RTI Elec | UL 746 | 60.0 °C |