PC D151-WH9G667 SABIC INNOVATIVE NANSHA
LEXAN™
Electronic and Electrical Applications,Plastic bag
Glass fiber reinforced,Non chloro non bromine fl
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/D151-WH9G667 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 13 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 710 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 50 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 22.0 J |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/D151-WH9G667 |
|---|---|---|---|
| dielectric constant | 1.90GHz | 内部方法 | 3.06 |
| Dissipation Factor | 5.00GHz | 内部方法 | 6.9E-03 |
| 1.90GHz | 内部方法 | 6.5E-03 | |
| 10.0GHz | 内部方法 | 6.9E-03 | |
| dielectric constant | 1.10GHz | 内部方法 | 3.07 |
| Dissipation Factor | 1.10GHz | 内部方法 | 6.7E-03 |
| dielectric constant | 10.0GHz | 内部方法 | 3.05 |
| 5.00GHz | 内部方法 | 3.06 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/D151-WH9G667 |
|---|---|---|---|
| fracture | ISO 527-2/5 | 82.0 Mpa | |
| ASTM D638 | 3.6 % | ||
| --6 | ISO 178 | 133 Mpa | |
| --5 | ISO 178 | 4010 Mpa | |
| fracture | ASTM D638 | 83.0 Mpa | |
| 50.0mm span | ASTM D790 | 4070 Mpa | |
| --1 | ASTM D638 | 4400 Mpa | |
| fracture | ISO 527-2/5 | 3.6 % | |
| Fracture, 50.0mm span | ASTM D790 | 131 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/D151-WH9G667 |
|---|---|---|---|
| UL flame retardant rating | 0.600mm | UL 94 | V-0 |
| 0.400mm | UL 94 | V-1 | |
| 0.300mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/D151-WH9G667 |
|---|---|---|---|
| melt mass-flow rate | 300°C/2.16kg | ASTM D1238 | 29 g/10min |
| Shrinkage rate | TD:24小时 | ASTM D955 | 0.30-0.50 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 13.0 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.040 % |
| 饱和,23°C | ISO 62 | 0.080 % | |
| Shrinkage rate | MD:24小时 | ASTM D955 | 0.30-0.50 % |
| Melt volume flow rate | 300°C/2.16kg | ISO 1133 | 27.0 cm3/10min |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 14 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/D151-WH9G667 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:23到80°C | ISO 11359-2 | 7.7E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 121 °C |
| Linear coefficient of thermal expansion | MD:23到80°C | ISO 11359-2 | 3.4E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 117 °C |