PC SABIC INNOVATIVE US XHT3143T-NA8E055T

Injection grade

US$ 6,610 / MT

FOB Guangzhou port, China

injection	Test Condition	Test Method	SABIC INNOVATIVE US/XHT3143T-NA8E055T
Back pressure			0.300 to 0.700 Mpa
Temperature at the front of the material cylinder			290 to 325 °C
Spray nozzle temperature			285 to 320 °C
Screw speed			40 to 90 rpm
Mold temperature			95 to 130 °C
Exhaust hole depth			0.025 to 0.080 mm
Processing (melt) temperature			290 to 325 °C
drying temperature			135 °C
Suggested injection volume			40 to 60 %
Temperature in the middle of the barrel			280 to 310 °C
drying time			4.0 to 6.0 hr
Suggested maximum moisture content			0.020 %
Temperature at the rear of the barrel			270 to 300 °C
thermal performance	Test Condition	Test Method	SABIC INNOVATIVE US/XHT3143T-NA8E055T
Vicat softening temperature	--	ISO 306/B50	168 °C
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	6.0E-5 cm/cm/°C
Linear coefficient of thermal expansion		Across Flow : -40°C	ISO 11359-2	6.0E-5 cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	156 °C
Hot deformation temperature		1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Af	152 °C
Vicat softening temperature	--	ASTM D15259	170 °C
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	166 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.0E-5 cm/cm/°C
mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE US/XHT3143T-NA8E055T
bending strength	--4,5	ISO 178	80.0 Mpa
elongation	Yield	ISO 527-2/50	6.0 %
elongation		Yield2	ASTM D638	6.0 %
Bending modulus	50.0 mm Span3	ASTM D790	2600 Mpa
bending strength	Yield, 50.0 mm Span3	ASTM D790	120 Mpa
tensile strength	Break	ISO 527-2/50	60.0 Mpa
elongation	Break2	ASTM D638	70 %
tensile strength	Yield2	ASTM D638	70.0 Mpa
tensile strength		Yield	ISO 527-2/50	70.0 Mpa
Tensile modulus	--1	ASTM D638	2700 Mpa
Bending modulus	--4	ISO 178	2500 Mpa
Tensile modulus	--	ISO 527-2/1	2500 Mpa
elongation	Break	ISO 527-2/50	70 %
tensile strength	Break2	ASTM D638	55.0 Mpa
impact performance	Test Condition	Test Method	SABIC INNOVATIVE US/XHT3143T-NA8E055T
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.0 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	无断裂
Dart impact	23°C, Total Energy	ASTM D3763	68.0 J
Charpy Notched Impact Strength	23°C	ISO 179/1eA	11 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength		23°C	ISO 180/1U	无断裂
Physical properties	Test Condition	Test Method	SABIC INNOVATIVE US/XHT3143T-NA8E055T
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.30 %
melt mass-flow rate	330°C/2.16 kg	ASTM D1238	33 g/10 min
Water absorption rate	Saturation, 23°C	ISO 62	0.30 %
Melt Volume Flow Rate (MVR)	330°C/2.16 kg	ISO 1133	30.0 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.60 - 0.90 %