PBT S 4090 G6 BASF GERMANY
Ultradur® 
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodBASF GERMANY/S 4090 G6
Hot deformation temperature1.8MPa,UnannealedASTM D648177 °C
0.45MPa,UnannealedISO 75-2/B210 °C
1.8MPa,UnannealedISO 75-2/A175 °C
0.45MPa,UnannealedASTM D648210 °C
Linear coefficient of thermal expansionMD4E-05 cm/cm/°C
Melting temperatureASTM D3418223 °C
ISO 3146223 °C
RTI Elec3.0mmUL 746130 °C
1.5mmUL 746130 °C
0.69mmUL 746130 °C
RTI Imp1.5mmUL 74690.0 °C
0.69mmUL 74690.0 °C
3.0mmUL 74690.0 °C
RTI Str3.0mmUL 746130 °C
0.69mmUL 746130 °C
1.5mmUL 746130 °C
mechanical propertiesTest ConditionTest MethodBASF GERMANY/S 4090 G6
Bending modulus23°CISO 1788300 Mpa
23°CASTM D7908270 Mpa
bending strength23°CASTM D790194 Mpa
elongationBreak,23°CASTM D6382.2 %
Tensile creep modulus1hrISO 899-17600 Mpa
1000hrISO 899-16700 Mpa
Tensile modulus23°CISO 527-29700 Mpa
Tensile strainBreak,80°CISO 527-23.6 %
Break,23°CISO 527-22.2 %
Break,150°CISO 527-24.8 %
Break,120°CISO 527-25.9 %
Break,-40°CISO 527-22.4 %
tensile strengthBreak,23°CISO 527-2125 Mpa
Break,120°CISO 527-247.0 Mpa
Break,23°CASTM D638125 Mpa
Break,-40°CISO 527-2195 Mpa
Break,150°CISO 527-235.0 Mpa
Break,80°CISO 527-279.0 Mpa
Electrical performanceTest ConditionTest MethodBASF GERMANY/S 4090 G6
Compared to the anti leakage trace indexIEC 60112PLC 1
Dielectric constant1MHzIEC 602503.70
100HzIEC 602503.80
Dissipation factor1MHzIEC 602500.018
100HzIEC 602503E-03
Surface resistivityASTM D2571E+14 ohms
IEC 600931E+14 ohms
Volume resistivityIEC 60093>1.0E+13 ohms·cm
1.50mmASTM D257>1.0E+13 ohms·cm
Physical propertiesTest ConditionTest MethodBASF GERMANY/S 4090 G6
densityISO 11831.47 g/cm³
ASTM D7921.47 g/cm³
Melt Volume Flow Rate (MVR)275°C/2.16kgISO 113320.0 cm3/10min
Shrinkage rateMDISO 294-40.29 %
TDISO 294-40.75 %
MD：3.18mm0.30 %
Viscosity value降低的粘度ISO 1628105.0 ml/g
Water absorption rateSaturationASTM D5700.40 %
Equilibrium,23°C,50%RHISO 620.20 %
Equilibrium,50%RHASTM D5700.20 %
Saturation,23°CISO 620.40 %
impact performanceTest ConditionTest MethodBASF GERMANY/S 4090 G6
Charpy Notched Impact Strength23°CISO 1799.0 kJ/m²
Impact strength of cantilever beam gap23°CASTM D25685 J/m
-40°CASTM D25669 J/m
Impact strength of simply supported beam without notch-30°CISO 17950 kJ/m²
23°CISO 17959 kJ/m²
flammabilityTest ConditionTest MethodBASF GERMANY/S 4090 G6
UL flame retardant rating3.0mmUL 94HB
0.69mmUL 94HB
1.5mmUL 94HB