Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA612 FS 4104 A SCHULMAN USA
SCHULAMID®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | A SCHULMAN USA/FS 4104 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃23°C | ISO 179/1eU | No Break |
| -30℃-30°C | ISO 179/1eU | No Break |
| Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/FS 4104 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 1200 Mpa | |
| Nominal tensile fracture strain | ISO 527-2/1A/50 | > 200 % | |
| tensile strength | 断裂断裂 | ISO 527-2/1A/50 | 40 Mpa |
| Electrical performance | Test Condition | Test Method | A SCHULMAN USA/FS 4104 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A解决方案 A | IEC 60112 | V |
| Flame retardant performance | Test Condition | Test Method | A SCHULMAN USA/FS 4104 |
|---|---|---|---|
| GWIT | 1.5 mm1.5 mm | IEC 60695-2-13 | 750 °C |
| Flammability level | UL 94 | HB | |
| Glow wire combustion index (GWFI) | 3.0 mm3.0 mm | IEC 60695-2-12 | 725 °C |
| burning rate | ISO 3795 | 30 mm/min | |
| GWIT | 3 mm3.0 mm | IEC 60695-2-13 | 750 °C |
| Glow wire combustion index (GWFI) | 1.5 mm1.5 mm | IEC 60695-2-12 | 725 °C |
| physical property | Test Condition | Test Method | A SCHULMAN USA/FS 4104 |
|---|---|---|---|
| density | ISO 1183/A | 1.01 g/cm³ |
| Thermal performance | Test Condition | Test Method | A SCHULMAN USA/FS 4104 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa，未退火1.8 MPa，未退火，HDT | ISO 75-2/Af | 55 °C |
| 0.45 MPa，未退火0.45 MPa，未退火，HDT | ISO 75-2/Bf | 70 °C | |
| vicat | A50-- | ISO 306/A50 | 200 °C |
| B50-- | ISO 306 | 100 °C |