PPO FE1630PW 73701 SABIC EU
NORYL™
Automotive interior parts、Electrical applications
High temperature resistan、High mobility、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC EU/FE1630PW 73701 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 30 kJ/m² |
| 23°C | ISO 180/1U | 30 kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| -30°C | ISO 179/1eA | 9.0 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 30 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 30 kJ/m² |
| hardness | Test Condition | Test Method | SABIC EU/FE1630PW 73701 |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 240 Mpa |
| Mechanical properties | Test Condition | Test Method | SABIC EU/FE1630PW 73701 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 9600 Mpa | |
| ASTM D638 | 9580 Mpa | ||
| tensile strength | 断裂 | ISO 527-2/5 | 133 Mpa |
| elongation | 断裂 | ASTM D638 | 2.4 % |
| bending strength | ISO 178 | 192 Mpa | |
| Flexural modulus | ISO 178 | 8120 Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 65.0 mg |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.5 % |
| tensile strength | 断裂 | ASTM D638 | 134 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 7760 Mpa |
| physical property | Test Condition | Test Method | SABIC EU/FE1630PW 73701 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.10-0.30 % |
| melt mass-flow rate | 300°C/5.0kg | ASTM D1238 | 9.0 g/10min |
| Melt volume flow rate | 300°C/10.0kg | ISO 1133 | 30.0 cm3/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.20-0.50 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.060 % |
| 饱和,23°C | ISO 62 | 0.20 % |
| Thermal performance | Test Condition | Test Method | SABIC EU/FE1630PW 73701 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Be | 150 °C |
| vicat | -- | ISO 306/B120 | 158 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| vicat | -- | ISO 306/A50 | 165 °C |
| -- | ISO 306/B50 | 154 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 3E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Ae | 145 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 145 °C |