PA6 Padermid 6 GF30 N TKC Kunststoffe e.K.
--
Applications in electrical, electronic applications, casings, automotive fields, gears
Filler, glass fiber reinforced material, 30%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Electrical performance | Test Condition | Test Method | TKC Kunststoffe e.K./Padermid 6 GF30 N |
---|---|---|---|
dielectric strength | IEC 60243-1 | 20 KV/mm | |
Dissipation Factor | 相对漏电起痕指数 | STN346468.00 | 575 V |
Surface Resistivity | IEC 60093 | 8E+13 Ω.cm | |
Volume resistivity | IEC 60093 | 5E+13 Ω.cm |
Mechanical properties | Test Condition | Test Method | TKC Kunststoffe e.K./Padermid 6 GF30 N |
---|---|---|---|
Flexural modulus | 23°C | ISO 178 | 7600 MPa |
Tensile modulus | 23°C | ISO 527-2 | 8900 MPa |
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 12 kJ/m² |
tensile strength | 23°C | ISO 527-2 | 170 MPa |
elongation at break | 23°C | ISO 527-2 | 3 % |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 65 kJ/m² |
bending strength | 23°C | ISO 178 | 200 MPa |
Flame retardant performance | Test Condition | Test Method | TKC Kunststoffe e.K./Padermid 6 GF30 N |
---|---|---|---|
Relative temperature of heating wire | IEC 60695-2-13 | 650 °C | |
UL flame retardant rating | UL -94 | HB . |
physical property | Test Condition | Test Method | TKC Kunststoffe e.K./Padermid 6 GF30 N |
---|---|---|---|
Water absorption rate | DI53495 | 1.8 % | |
density | ISO 1183 | 1.33 g/cm³ | |
Shrinkage rate | STN640808.00 | 0.45 % |
Thermal performance | Test Condition | Test Method | TKC Kunststoffe e.K./Padermid 6 GF30 N |
---|---|---|---|
vicat | ISO 306/B50 | 210 °C | |
Linear coefficient of thermal expansion | 熔融温度 | ISO 3146 | 220 °C |