Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL1433T SABIC INNOVATIVE US
LEXAN™
Automotive sector、Electronic and Electrical、Plastic bag
Middle flow、High ductility at low tem、Short molding cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/EXL1433T
Melt Volume-Flow Rate (MVR)
300°C/1.2kg
ISO1133
cm3/10min
9
Melt mass flow rate
300°C/1.2kg
ASTMD1238
g/10min
1
Shrinkage rate
MD：3.20mm
内部方法
%
0
Shrinkage rate
TD：3.20mm
内部方法
%
0
Shrinkage rate
MD:3.20mm
内部方法
%
0
Shrinkage rate
TD:3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/EXL1433T
--
ASTMD638
Mpa
2
--
ISO527-2/1
Mpa
2
--
ISO178
Mpa
2
--
ISO178
Mpa
9
23°C
ISO180/1A
kJ/m²
6
23°C
ASTMD256
J/m
8
-30°C
ASTMD256
J/m
8
-30°C
ISO180/1A
kJ/m²
4
50.0mm span
ASTMD790
Mpa
2
Fracture
ASTMD638
Mpa
6
crack
ISO527-2/50
Mpa
6
Fracture
ASTMD638
%
1
crack
ISO527-2/50
%
1
The impact strength of a simply supported beam with a notch of
-30°C
ISO179/1eA
kJ/m²
5
The impact strength of a simply supported beam with a notch of
23°C
ISO179/1eA
kJ/m²
7
Impact strength of simply supported beam gap
-30°C
ISO179/1eA
kJ/m²
5
Impact strength of simply supported beam gap
23°C
ISO179/1eA
kJ/m²
7
Tensile modulus
ASTMD638
Mpa
2
Tensile modulus
ISO527-2/1
Mpa
2
tensile strength
屈服
ASTMD638
Mpa
5
tensile strength
屈服
ISO527-2/50
Mpa
5
tensile strength
断裂
ASTMD638
Mpa
6
tensile strength
断裂
ISO527-2/50
Mpa
6
Surrender
ASTMD638
%
5
yield
ISO527-2/50
%
5
Surrender
ASTMD638
Mpa
5
yield
ISO527-2/50
Mpa
5
Yield, 50.0mm span
ASTMD790
Mpa
9
elongation
屈服
ASTMD638
%
5
elongation
屈服
ISO527-2/50
%
5
elongation
断裂
ASTMD638
%
1
elongation
断裂
ISO527-2/50
%
1
Bending modulus
50.0mm跨距
ASTMD790
Mpa
2
Bending modulus
ISO178
Mpa
2
bending strength
屈服,50.0mm跨距
ASTMD790
Mpa
9
Bending strength 5,
ISO178
Mpa
9
Suspended wall beam gap impact strength
-30°C
ISO180/1A
kJ/m²
4
Suspended wall beam gap impact strength
23°C
ISO180/1A
kJ/m²
6
Dart impact equipped with measuring instruments
-30°C,TotalEnergy
ASTMD3763
J
8
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
8
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/EXL1433T
--
ASTMD1525,ISO306/B501116
°C
1
--
ISO306/B120
°C
1
1.8MPa, unannealed, 3.20mm
ASTMD648
°C
1
1.8MPa, unannealed, 64.0mm span
ISO75-2/Af
°C
1
RTI
UL746
°C
1
RTIElec
UL746
°C
1
RTIStr
UL746
°C
1
Horizontal: 23 to 80 ° C
ISO11359-2
cm/cm/°C
7
Horizontal: -40 to 95 ° C
ASTME831
cm/cm/°C
7
Flow: 23 to 80 ° C
ISO11359-2
cm/cm/°C
7
Flow: -40 to 95 ° C
ASTME831
cm/cm/°C
7
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
1
vicat softening point
ASTMD152510
°C
1
vicat softening point
--
ISO306/B50
°C
1
vicat softening point
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：-40到95°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
MD：23到80°C
ISO11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：-40to95°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：23to80°C
ISO11359-2
cm/cm/°C
7
Electrical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/EXL1433T
Surface resistivity
ASTMD257
ohms
>
Volume resistivity
ASTMD257
ohms·cm
>
flammability
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/EXL1433T
Hot filament ignition temperature
0.8mm
IEC60695-2-13
°C
8
Hot filament ignition temperature
3.0mm
IEC60695-2-13
°C
8
Hot filament ignition temperature
0.800mm
IEC60695-2-13
°C
8
Hot filament ignition temperature
3.00mm
IEC60695-2-13
°C
8
Burning wire flammability index
3.00mm
IEC60695-2-12
°C
9
Burning wire flammability index
3.0mm
IEC60695-2-12
°C
9
optical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/EXL1433T
Light transmittance
2540µm
ASTMD1003
%
8
Haze
2540µm
ASTMD1003
%
3