Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 191 ASAHI JAPAN
--
--
High impact resistance、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodASAHI JAPAN/191
Rockwell hardnessR计秤,2.50mm103
R计秤ISO 2039-2109
Basic performanceTest ConditionTest MethodASAHI JAPAN/191
melt mass-flow rate200℃,21.6kg28 g/10min
Mechanical propertiesTest ConditionTest MethodASAHI JAPAN/191
Rockwell hardness111 R
bending strengthASTM D790/ISO 17866 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gapASTM D256/ISO 179157 kg·cm/cm(J/M)ft·lb/in
tensile strength 屈服ISO 527-2/5044.8 Mpa
Flexural modulusASTM D790/ISO 1782370 kg/cm²(MPa)[Lb/in²]
bending strengthISO 17872.6 Mpa
Impact strength of cantilever beam gap23℃157 KJ/m
Flexural modulusISO 1782400 Mpa
2.45 GPa
elongation at breakASTM D638/ISO 52743 %
tensile strength 76 Mpa
ASTM D638/ISO 52750 kg/cm²(MPa)[Lb/in²]
otherTest ConditionTest MethodASAHI JAPAN/191
characteristic中冲击
Physical propertiesTest ConditionTest MethodASAHI JAPAN/191
densityASTM D792/ISO 11831.05
melt mass-flow rateASTM D1238/ISO 113325 g/10min
flammabilityTest ConditionTest MethodASAHI JAPAN/191
UL flame retardant rating1.5mmUL 94HB
physical property Test ConditionTest MethodASAHI JAPAN/191
Shrinkage rateMDASTM D9550.40-0.60 %
Melt volume flow rate220°C/10.0kgISO 113326.9 cm3/10min
melt mass-flow rate220°C/10.0kgISO 113326 g/10min
Thermal performanceTest ConditionTest MethodASAHI JAPAN/191
vicatISO 306/B99.5 °C
Heat distortion temperatureHDTASTM D648/ISO 7587 ℃（℉）
vicatASTM D1525/ISO R306105 ℃（℉）
106 °C
Heat distortion temperature1.0MPa，HDT81 °C
1.8MPa,未退火，HDTISO 75-2/A80.1 °C
RTI ImpUL 74660.0 °C
RTIUL 74660.0 °C
ball-indentation hardnessEMAC85 °C
RTI ElecUL 74660.0 °C