Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PC AZ1900T IDEMITSU JAPAN
TARFLON™
Automotive Applications,Home appliance components
Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
hardness | Test Condition | Test Method | IDEMITSU JAPAN/AZ1900T |
---|---|---|---|
Rockwell hardness | M 计秤 | ISO 2039-2 | 50 |
R 计秤 | ISO 2039-2 | 120 | |
R计秤 | ISO 2039-2 | 120 | |
M计秤 | ISO 2039-2 | 50 |
Supplementary Information | Test Condition | Test Method | IDEMITSU JAPAN/AZ1900T |
---|---|---|---|
ISO Shortcut | >PC< |
Electrical performance | Test Condition | Test Method | IDEMITSU JAPAN/AZ1900T |
---|---|---|---|
dielectric strength | IEC 60243-1 | 30 KV/mm | |
dielectric constant | 1MHz | IEC 60250 | 2.85 |
Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
Volume resistivity | ASTM D257/IEC 60093 | - Ω.cm | |
dielectric constant | 1 MHz | IEC 60250 | 2.85 |
Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/AZ1900T |
---|---|---|---|
Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 80 kg·cm/cm(J/M)ft·lb/in | |
Flexural modulus | ASTM D790/ISO 178 | 2400 kg/cm²(MPa)[Lb/in²] | |
Charpy Notched Impact Strength | ISO 179 | 65 kJ/m² | |
elongation | ASTM D638/ISO 527 | 64 % | |
elongation at break | ASTM D638/ISO 527 | 92 % | |
Rockwell hardness | ASTM D785 | - | |
elongation at break | ISO 527-2 | 70 % | |
tensile strength | ASTM D638/ISO 527 | 68 kg/cm²(MPa)[Lb/in²] | |
Nominal tensile fracture strain | ISO 527-2 | 95 % | |
bending strength | ISO 178 | 90.0 Mpa | |
Flexural modulus | ISO 178 | 2300 Mpa | |
Tensile modulus | ASTM D638/ISO 527 | 2300 kg/cm²(MPa)[Lb/in²] | |
tensile strength | 屈服 | ISO 527-2 | 65.0 Mpa |
optical performance | Test Condition | Test Method | IDEMITSU JAPAN/AZ1900T |
---|---|---|---|
transmissivity | ISO 13468-1 | 85.0to89.0 % |
other | Test Condition | Test Method | IDEMITSU JAPAN/AZ1900T |
---|---|---|---|
characteristic | 高流动型 |
Physical properties | Test Condition | Test Method | IDEMITSU JAPAN/AZ1900T |
---|---|---|---|
Shrinkage rate | ASTM D955 | 0.5-0.7 % | |
density | ASTM D792/ISO 1183 | 1.20 | |
melt mass-flow rate | ASTM D1238/ISO 1133 | - g/10min | |
Water absorption rate | ASTM D570/ISO 62 | - % |
flammability | Test Condition | Test Method | IDEMITSU JAPAN/AZ1900T |
---|---|---|---|
ISO 9660 | >PC< | ||
UL flame retardant rating | 1.5 mm | UL 94 | V-0 |
1.5mm | UL 94 | V-0 |
physical property | Test Condition | Test Method | IDEMITSU JAPAN/AZ1900T |
---|---|---|---|
Melt volume flow rate | MVR | ISO 1133 | 5 cm3/10min |
Shrinkage rate | TD:2.00mm | 内部方法 | 0.50-0.70 % |
Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 18.0 cm3/10min |
spiral flow length | 内部方法 | 29.0 CM | |
Shrinkage rate | MD: 2.00 mm | 内部方法 | 0.5-0.7 % |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.23 % |
Shrinkage rate | 流量 : 2.00 mm | 内部方法 | 0.50 - 0.70 % |
TD | 内部方法 | 0.5-0.7 % | |
MD:2.00mm | 内部方法 | 0.50-0.70 % | |
横向流量 : 2.00 mm | 内部方法 | 0.50 - 0.70 % | |
Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.23 % |
Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 5.00 cm3/10min |
Water absorption rate | 平衡, 23℃, 50% RH | ISO 62 | 0.23 % |
Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/AZ1900T |
---|---|---|---|
Combustibility (rate) | UL 94 | V-0/1.5mm | |
Heat distortion temperature | 1.8 MPa, 未退火,HDT | ISO 75-2/A | 125 °C |
UL flame retardant rating | 4.00 mm | UL 94 | 5VA |
RTI Str | UL 746 | 80.0 °C | |
RTI | UL 746 | 80.0 °C | |
Linear coefficient of thermal expansion | ASTM D696 | 0.000065 cm/cm/℃ | |
ASTM D696/ISO 11359 | - mm/mm.℃ | ||
Heat distortion temperature | HDT | ASTM D648/ISO 75 | 131 ℃(℉) |
vicat | ASTM D1525/ISO R306 | - ℃(℉) | |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 140 °C |
1.8MPa,未退火,HDT | ISO 75-2/A | 125 °C | |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.5E-05 cm/cm/°C |
UL flame retardant rating | 1.50 mm | UL 94 | V-0 |
RTI Imp | UL 746 | 80.0 °C | |
Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 6.5E-5 cm/cm/°C |
RTI Elec | UL 746 | 80.0 °C |
injection | Test Condition | Test Method | IDEMITSU JAPAN/AZ1900T |
---|---|---|---|
drying time | 5.0 to 8.0 hr | ||
Temperature in the middle of the barrel | 260 to 300 °C | ||
Temperature at the rear of the barrel | 260 to 300 °C | ||
drying temperature | 120 °C | ||
Temperature at the front of the material cylinder | 260 to 300 °C | ||
Temperature | 80 to 120 °C |