PC/PET X7200-NA9A008 SABIC INNOVATIVE US
XYLEX™
Industrial applications、Electronic field、Electrical field、Automotive sector
UV resistance、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/X7200-NA9A008 |
|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 1.1E-04 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 73.4 °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 103 °C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 110 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| MD：-40到40°C | ISO11359-2 | 9.9E-05 cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 71.1 °C |
| Vicat Softening Temperature | ASTMD152510 | 146 °C | |
| -- | ISO306/B120 | 107 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 9.9E-05 cm/cm/°C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/X7200-NA9A008 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 1450 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 28.0 Mpa |
| Tensile Elongation | ASTMD638 | 130 % | |
| Tensile Strain | ISO527-2/50 | 120 % | |
| Tensile Modulus | ISO527-2/1 | 1670 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 33.8 Mpa |
| Flexural Modulus | ISO178 | 1610 Mpa | |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 49.0 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 10 % |
| Tensile Stress | ISO527-2/50 | 34.0 Mpa | |
| Tensile Strain | 8.2 % | ||
| Flexural Strength | ISO178 | 48.0 Mpa | |
| Tensile Modulus | ASTMD638 | 1240 Mpa | |
| Tensile Strength | 断裂 | 27.6 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/X7200-NA9A008 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.020 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.60to0.80 % |
| Melt Volume flow Rate | 260°C/5.0kg | ISO1133 | 18.0 cm3/10min |
| Modeling Shrinkage | TD：3.20mm | 内部方法 | 0.60to0.80 % |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.050 % |
| Melt Mass-Flow Rate | 260°C/5.0kg | ASTMD1238 | 16 g/10min |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/X7200-NA9A008 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 8.0 kJ/m² |
| Unnotched Izod Impact Strength | ISO180/1U | NoBreak | |
| Charpy Notched Impact Strength | ISO179/1eA | 6.1 kJ/m² | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 36.2 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 12 kJ/m² |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 80 kJ/m² |
| 23°C | NoBreak | ||
| Unnotched Izod Impact Strength | ISO180/1U | NoBreak | |
| Notched Izod Impact Strength | ISO180/1A | 14 kJ/m² |