Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA12 SCL36 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electrical appliances、Plastic bag
lubrication、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/SCL36 |
|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 6 | ISO 75-2/Bf | 177 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 6 | ISO 75-2/Af | 170 °C | |
| Linear thermal expansion coefficient | 横向 : -30 到 30°C | ASTM D696 | 6.3E-5 cm/cm/°C |
| 流动 : -30 到 30°C | 2.9E-5 cm/cm/°C | ||
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 173 °C |
| 0.45 MPa, 未退火, 3.20 mm | 178 °C |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE US/SCL36 |
|---|---|---|---|
| Suggested Max Moisture | 0.12 到 0.20 % | ||
| Middle Temperature | 220 到 230 °C | ||
| Processing (Melt) Temp | 225 到 240 °C | ||
| Drying Time | 4.0 hr | ||
| Rear Temperature | 215 到 225 °C | ||
| Drying Temperature | 80 °C | ||
| Front Temperature | 225 到 240 °C | ||
| Back Pressure | 0.200 到 0.300 Mpa | ||
| Mold Temperature | 70 到 80 °C | ||
| Screw Speed | 30 到 60 rpm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/SCL36 |
|---|---|---|---|
| Modeling Shrinkage | 流动 : 24小时 | ASTM D955 | 0.040 到 0.060 % |
| Moisture Absorption | 24 hr, 50% RH | ASTM D570 | 0.090 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.14 % | |
| Modeling Shrinkage | 横向流动 : 24小时 | ASTM D955 | 0.40 到 0.60 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/SCL36 |
|---|---|---|---|
| Flexural Stress | -- | ISO 178 | 206 Mpa |
| Tensile Modulus | ISO 527-2/1 | 19400 Mpa | |
| Tensile Elongation | 断裂 2 | ASTM D638 | 1.9 % |
| Specific Wear Rate | ASTM D3702 | 0.0 4.4E+6 10^-8 mm³/N·m | |
| Tensile Elongation | 断裂 | ISO 527-2/5 | 1.0 % |
| Tensile Strength | 130 Mpa | ||
| Coefficient of Friction | Dynamic | ASTM D3702 | 0.41 |
| Flexural Modulus | 50.0 mm 跨距 3 | ASTM D790 | 15800 Mpa |
| Tensile Modulus | -- 1 | ASTM D638 | 21400 Mpa |
| Flexural Stress | 断裂, 50.0 mm 跨距 3 | ASTM D790 | 214 Mpa |
| Flexural Modulus | -- 4 | ISO 178 | 16500 Mpa |
| Flexural Stress | 屈服, 50.0 mm 跨距 3 | ASTM D790 | 215 Mpa |
| Coefficient of Friction | Static | ASTM D3702 | 0.30 |
| Tensile Strength | 断裂 2 | ASTM D638 | 157 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/SCL36 |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 690 J/m |
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 14.0 J |
| -- | ISO 6603-2 | 4.00 J | |
| Unnotched Izod Impact Strength | 23°C 6 | ISO 180/1U | 39 kJ/m² |