PC/ABS AC2100 FCFC TAIWAN
TAIRILOY®
Automotive sector,Phone,Medical devices,Electronic field,Electrical field,automotive industry ,Phone,Electrical housing,Electrical/Electronic Applications,Medical devices
High impact resistance,Thermal stability,Dimensional stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | FCFC TAIWAN/AC2100 |
|---|---|---|---|
| melt mass-flow rate | 240℃/5kg | ASTM D1238，ISO 1133 | 5.5 g/10min |
| Mechanical properties | Test Condition | Test Method | FCFC TAIWAN/AC2100 |
|---|---|---|---|
| Shrinkage rate | Flow 3.2mm | ASTM D955 | 0.4－0.6 % |
| bending strength | 23℃ | ISO 178 | 84 MPa |
| Impact strength of cantilever beam gap | 23℃,6.35mm | ISO 180，ASTM D256 | 637 J/m |
| Flexural modulus | 23℃ | ASTM D790，ISO 178 | 2450 MPa |
| tensile strength | 23℃，屈服 | ASTM D638，ISO 527-2 | 52 MPa |
| bending strength | 23℃ | ASTM D790 | 83.4 MPa |
| physical property | Test Condition | Test Method | FCFC TAIWAN/AC2100 |
|---|---|---|---|
| density | ASTM D792 | 1.16 g/cm | |
| Rockwell hardness | R-Scale | ASTM D785，ISO 2039-2 | 113 |
| Thermal performance | Test Condition | Test Method | FCFC TAIWAN/AC2100 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,unannealed，6.35mm，HDT | ASTM D648 | 110 ℃ |
| vicat | ISO 360A，ASTM 1525 | 140 ℃ | |
| Heat distortion temperature | 1.8MPa,unannealed，6.35mm Span，HDT | ISO 75-2/A | 110 ℃ |
| UL flame retardant rating | UL 94 | HB |