PPO GTX975 SABIC INNOVATIVE SHANGHAI
NORYL GTX™ 
Industrial machinery,Electrical applications
Hydrolysis resistance,High temperature resistan,Dimensional stability,High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/GTX975
Ball Pressure TestH358/30ISO 2039-1125 Mpa
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/GTX975
Hot deformation temperature0.45MPa,Unannealed,100mmSpanISO 75-2/Be185 °C
Linear coefficient of thermal expansionMD:23to60°CISO 11359-25E-05 cm/cm/°C
TD:23to60°CISO 11359-26.5E-05 cm/cm/°C
Vicat softening temperature--ISO 306/B120200 °C
--ISO 306/B50195 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/GTX975
Bending modulusISO 1784000 Mpa
bending strengthISO 178110 Mpa
Tensile modulusISO 527-2/14200 Mpa
Tensile strainBreakISO 527-2/54.0 %
tensile strengthBreakISO 527-2/565.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/GTX975
Volume resistivityInternal Method1.0E+3-1.0E+4 ohms·cm
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/GTX975
Melt Volume Flow Rate (MVR)280°C/5.0kgISO 113310.0 cm3/10min
Shrinkage rateMD2Internal Method1.1-1.3 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/GTX975
Charpy Notched Impact Strength23°CISO 179/1eA3.5 kJ/m²
-30°CISO 179/1eA3.0 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A4.0 kJ/m²
23°CISO 180/1A4.0 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU35 kJ/m²
23°CISO 179/1eU40 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U40 kJ/m²
-30°CISO 180/1U35 kJ/m²