POM FX-11 MITSUBISHI THAILAND
Iupital™ 
Automotive sector、Electronic and Electrical
wear resistant、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI THAILAND/FX-11
Charpy Notched Impact Strength23°CISO 1797.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179200 kJ/m²
Mechanical propertiesTest ConditionTest MethodMITSUBISHI THAILAND/FX-11
Tensile modulusISO 527-22700 Mpa
Nominal tensile fracture strainISO 527-235 %
bending strengthISO 17881.0 Mpa
Flexural modulusISO 1782500 Mpa
Tensile strain屈服ISO 527-29.0 %
tensile strength 屈服ISO 527-255.0 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI THAILAND/FX-11
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 0
dielectric strength1.00mmIEC 60243-136 KV/mm
Volume resistivityIEC 600931E+14 ohms·cm
dielectric strength3.00mmIEC 60243-119 KV/mm
Surface ResistivityIEC 600931E+16 ohms
flammabilityTest ConditionTest MethodMITSUBISHI THAILAND/FX-11
UL flame retardant rating0.8mmUL 94HB
physical property Test ConditionTest MethodMITSUBISHI THAILAND/FX-11
Melt volume flow rate190°C/2.16kgISO 11338.60 cm3/10min
Water absorption rate平衡,23°C,50%RHISO 620.22 %
densityISO 11831.39 g/cm³
melt mass-flow rate190°C/2.16kgISO 113310 g/10min
Shrinkage rateMD：3.00mm2.1 %
Thermal performanceTest ConditionTest MethodMITSUBISHI THAILAND/FX-11
melting temperatureISO 11357-3166 °C
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B156 °C
1.8MPa,未退火，HDTISO 75-2/A95.0 °C
Linear coefficient of thermal expansionMDISO 11359-21.1E-04 cm/cm/°C
TDISO 11359-21.1E-04 cm/cm/°C