POM N2200G43 BASF GERMANY
Ultraform®
Fiber grade,Electrical field,Electronic field,Household appliances,Household appliances,Lighting fixtures,Automotive sector
Glass fiber reinforced,High rigidity,high strength,Filler: Glass fiber reinf,20% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/N2200G43 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.5 kJ/m² |
| -30°C | ISO 179/1eA | 7.5 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 50 kJ/m² |
| -30°C | ISO 179/1eU | 50 kJ/m² |
| Supplementary Information | Test Condition | Test Method | BASF GERMANY/N2200G43 |
|---|---|---|---|
| Automotive Materials | >1.00mm | FMVSS302 | Passed |
| ISOType | ISO 9988-1 | POM-K.M-GNR.02-003.GF20 |
| hardness | Test Condition | Test Method | BASF GERMANY/N2200G43 |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 164 Mpa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/N2200G43 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 85 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 4.10 |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| Dissipation Factor | 1MHz | IEC 60250 | 7E-03 |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/N2200G43 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 7200 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.0 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | 4500 Mpa |
| tensile strength | 断裂 | ISO 527-2 | 115 Mpa |
| flammability | Test Condition | Test Method | BASF GERMANY/N2200G43 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | BASF GERMANY/N2200G43 |
|---|---|---|---|
| Apparent density | 0.85 g/cm³ | ||
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 4.00 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.3 % |
| MD | ISO 294-4 | 1.0 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| 饱和,23°C | ISO 62 | 0.90 % | |
| density | ISO 1183 | 1.54 g/cm³ |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/N2200G43 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 168 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 5E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 161 °C |
| maximum service temperature | 短周期操作 | 110 °C |