Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A3GF33 AKRO-PLASTIC GERMANY
AKROMID®
Machine/mechanical compon、Engineering accessories、Application in the automo
Filler: Glass fiber reinf、33% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF33 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 80 kJ/m² |
| -30°C | ISO 179/1eU | 80 kJ/m² |
| Supplementary Information | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF33 |
|---|---|---|---|
| ReinforcementContent | ISO 1172 | 33 % |
| Electrical performance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF33 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+13 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+12 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF33 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 11500 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 210 Mpa |
| Tensile strain | 断裂 | ISO 527-2/5 | 3.0 % |
| flammability | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF33 |
|---|---|---|---|
| burning rate | 1.00mm | FMVSS302 | <100 mm/min |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF33 |
|---|---|---|---|
| moisture absorption | 70°C，62%RH | ISO 1110 | 1.8to2.0 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 4.7to5.3 % |
| Thermal performance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF33 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 260 °C |
| melting temperature | DIN EN11357-1 | 262 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 255 °C |
| 8.0MPa,未退火，HDT | ISO 75-2/C | 220 °C |