PBT+PET SCHULADUR® A1 GF 30 HF FR 1 美国舒尔曼
--
--
填料,玻璃纤维增强材料,30%,填料按重量,
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 美国舒尔曼/SCHULADUR® A1 GF 30 HF FR 1 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| -30°C | ISO 179/1eA | 7.0 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 46 kJ/m² |
| -30°C | ISO 179/1eU | 40 kJ/m² |
| Electrical performance | Test Condition | Test Method | 美国舒尔曼/SCHULADUR® A1 GF 30 HF FR 1 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| Volume resistivity | IEC 60093 | >1.0E+13 ohms·cm | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
| Mechanical properties | Test Condition | Test Method | 美国舒尔曼/SCHULADUR® A1 GF 30 HF FR 1 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 12000 MPa | |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 148 MPa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 2.0 % |
| flammability | Test Condition | Test Method | 美国舒尔曼/SCHULADUR® A1 GF 30 HF FR 1 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | V-0 |
| 0.75mm | UL 94 | V-0 | |
| 0.75mm | IEC 60695-11-10,-20 | V-0 | |
| 3.0mm | UL 94 | V-0 | |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 675 °C |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | V-0 |
| burning rate | 1.50mm,自动灭火 | ISO 3795 | 0.0 mm/min |
| Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 960 °C |
| 3.0mm | IEC 60695-2-12 | 960 °C | |
| 1.5mm | IEC 60695-2-12 | 960 °C | |
| burning rate | 0.750mm,Self-Extinguishing | ISO 3795 | 0.0 mm/min |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 675 °C |
| Limiting Oxygen Index | ISO 4589-2 | 34 % | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| burning rate | 3.00mm,自动灭火 | ISO 3795 | 0.0 mm/min |
| Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 675 °C |
| physical property | Test Condition | Test Method | 美国舒尔曼/SCHULADUR® A1 GF 30 HF FR 1 |
|---|---|---|---|
| density | ISO 1183/A | 1.68 g/cm³ | |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 54.0 cm³/10min |
| Thermal performance | Test Condition | Test Method | 美国舒尔曼/SCHULADUR® A1 GF 30 HF FR 1 |
|---|---|---|---|
| vicat | -- | ISO 306/A50 | 218 °C |
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 219 °C |
| vicat | -- | ISO 306/B50 | 190 °C |
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ISO 75-2/Af | 198 °C |