LLDPE SP2020 PRIME POLYMER JAPAN
EVOLUE™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | PRIME POLYMER JAPAN/SP2020 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179 | 无断裂 |
| hardness | Test Condition | Test Method | PRIME POLYMER JAPAN/SP2020 |
|---|---|---|---|
| 邵氏D | ISO868 | 54 |
| Basic performance | Test Condition | Test Method | PRIME POLYMER JAPAN/SP2020 |
|---|---|---|---|
| melt mass-flow rate | 190℃/2.16kg | ISO 1133 | 2.1 g/10min |
| Mechanical properties | Test Condition | Test Method | PRIME POLYMER JAPAN/SP2020 |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2 | 17.0 Mpa |
| Flexural modulus | ISO178 | 220 Mpa | |
| Tensile fracture strain | Injection Molded | ISO 527-2 | 350 % |
| Shore hardness | Shore D，Injection Molded | ISO 868 | 54 |
| Tensile strain | 断裂 | ISO527-2 | 350 % |
| Shear supported beam without notch impact strength | ISO 179 | No Break |
| other | Test Condition | Test Method | PRIME POLYMER JAPAN/SP2020 |
|---|---|---|---|
| 低温热封性、高速成型性 | |||
| purpose | 复合膜、工业用膜 |
| Physical properties | Test Condition | Test Method | PRIME POLYMER JAPAN/SP2020 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 915 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 2.1 g/10min |
| physical property | Test Condition | Test Method | PRIME POLYMER JAPAN/SP2020 |
|---|---|---|---|
| Resistance to environmental stress cracking | ASTMD1693 | >1000 hr | |
| melt mass-flow rate | 190°C/2.16kg | ISO1133 | 2.1 g/10min |
| Thermal performance | Test Condition | Test Method | PRIME POLYMER JAPAN/SP2020 |
|---|---|---|---|
| vicat | ISO 306 | 93 ℃ | |
| melting temperature | ISO11357-3 | 116 °C | |
| vicat | ISO306 | 93.0 °C | |
| melt mass-flow rate | ISO 11357-3 | 116 ℃ |