PARA Reny® 4001 Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Reny® 4001 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 5.2 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 19 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Corporation/Reny® 4001 |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2 | 124 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 0.90 % |
| Tensile modulus | ISO 527-2 | 17900 MPa | |
| Flexural modulus | ISO 178 | 16600 MPa | |
| bending strength | ISO 178 | 204 MPa |
| flammability | Test Condition | Test Method | Mitsubishi Chemical Corporation/Reny® 4001 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Corporation/Reny® 4001 |
|---|---|---|---|
| Melt volume flow rate | 275°C/2.16kg | ISO 1133 | 3.40 cm³/10min |
| Shrinkage rate | 0.38 % | ||
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.0 % |
| 饱和,23°C | ISO 62 | 0.090 % | |
| density | ISO 1183 | 1.50 g/cm³ | |
| melt mass-flow rate | 275°C/2.16kg | ISO 1133 | 5.0 g/10min |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Reny® 4001 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 236 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 224 °C |