Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA 9KY22130 HUV 4Plas
--
--
Filler, glass fiber reinforced material, 30%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 4Plas/ 9KY22130 HUV |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 9.0 kJ/m² |
| 23°C | ISO 180/1A | 11 kJ/m² |
| Mechanical properties | Test Condition | Test Method | 4Plas/ 9KY22130 HUV |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 2.5 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 120 MPa |
| Tensile modulus | 23°C | ISO 527-2/5 | 9500 MPa |
| Electrical performance | Test Condition | Test Method | 4Plas/ 9KY22130 HUV |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+14 ohms |
| flammability | Test Condition | Test Method | 4Plas/ 9KY22130 HUV |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | 4Plas/ 9KY22130 HUV |
|---|---|---|---|
| Shrinkage rate | MD | 0.40 % | |
| water content | ISO 960 | <800 ppm | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.10 % |
| density | ISO 1183 | 1.55 g/cm³ | |
| Shrinkage rate | TD | 0.70 % |
| Thermal performance | Test Condition | Test Method | 4Plas/ 9KY22130 HUV |
|---|---|---|---|
| melting temperature | ISO 11357 | 225 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 210 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 155 °C |