Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PA6 6 GF15 A SCHULMAN USA
SCHULAMID®
--
Filler: Glass fiber reinf、15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | A SCHULMAN USA/6 GF15 |
---|---|---|---|
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 45 kJ/m² |
-30°C | ISO 179/1eU | 40 kJ/m² |
hardness | Test Condition | Test Method | A SCHULMAN USA/6 GF15 |
---|---|---|---|
ball-indentation hardness | H358/30 | ISO 2039-1 | 174 Mpa |
Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/6 GF15 |
---|---|---|---|
Tensile modulus | ISO 527-2/1A/1 | 5800 Mpa | |
bending strength | ISO 178 | 170 Mpa | |
Flexural modulus | ISO 178 | 4300 Mpa | |
Bending Strain | ISO 178 | 6.5 % | |
tensile strength | 断裂 | ISO 527-2/1A/5 | 120 Mpa |
Tensile strain | 断裂 | ISO 527-2/1A/5 | 3.5 % |
flammability | Test Condition | Test Method | A SCHULMAN USA/6 GF15 |
---|---|---|---|
UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | HB |
Burning wire flammability index | 3.0mm | IEC 60695-2-12 | -- °C |
UL flame retardant rating | 0.75mm | IEC 60695-11-10,-20 | HB |
1.5mm | IEC 60695-11-10,-20 | HB | |
Burning wire flammability index | 1.5mm | IEC 60695-2-12 | -- °C |
burning rate | ISO 3795 | <100 mm/min |
physical property | Test Condition | Test Method | A SCHULMAN USA/6 GF15 |
---|---|---|---|
viscosity number | ISO 307 | 145 cm³/g |
Thermal performance | Test Condition | Test Method | A SCHULMAN USA/6 GF15 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/Af | 200 °C |
vicat | -- | ISO 306/A50 | 215 °C |
-- | ISO 306/B50 | 210 °C | |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/Bf | 210 °C |