AES+PC KumhoSunny PC/AES HEC0245 Shanghai KumhoSunny Plastics Co., Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | Shanghai KumhoSunny Plastics Co., Ltd./KumhoSunny PC/AES HEC0245 | |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 60 % |
| Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | 500 J/m |
| 23°C4 | ISO 180 | 45 kJ/m² | |
| Shrinkage rate | MD | ASTM D955 | 0.50to0.70 % |
| tensile strength | -- | ASTM D638 | 53.0 MPa |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 48 kJ/m² |
| density | -- | ISO 1183 | 1.12 g/cm³ |
| Flexural modulus | --2 | ISO 178 | 2000 MPa |
| bending strength | --2 | ISO 178 | 63.0 MPa |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 32 kJ/m² |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 100 °C |
| bending strength | -- | ASTM D790 | 70.0 MPa |
| melt mass-flow rate | 230°C/10.0kg | ASTM D1238 | 20 g/10min |
| tensile strength | -- | ISO 527-2/50 | 50.0 MPa |
| Flexural modulus | -- | ASTM D790 | 1900 MPa |
| Shrinkage rate | -- | ISO 294-4 | 0.50to0.70 % |
| physical property | Test Condition | Test Method | Shanghai KumhoSunny Plastics Co., Ltd./KumhoSunny PC/AES HEC0245 |
|---|---|---|---|
| density | -- | ASTM D792 | 1.08 g/cm³ |
| vicat | ISO 306/B50 | 110 °C |
| Thermal performance | Test Condition | Test Method | Shanghai KumhoSunny Plastics Co., Ltd./KumhoSunny PC/AES HEC0245 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火5，HDT | ISO 75-2/A | 96.0 °C |