Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 RL-4530 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electronic and electrical accessories,Automotive components,Casters
High temperature resistan,resist fatigue
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/RL-4530 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 380 J/m |
| 23°C6 | ISO 180/1U | 26 kJ/m² | |
| Dart impact | 23°C, Energy at Peak | ASTM D3763 | 1.00 J |
| -- | ISO 6603-2 | 0.00 J |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/RL-4530 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距6，HDT | ISO 75-2/Bf | 221 °C |
| Linear coefficient of thermal expansion | 横向 : -40°C | ISO 11359-2 | 9.6E-5 cm/cm/°C |
| 流动 : -40 到 40°C | ISO 11359-2 | 9.1E-5 cm/cm/°C | |
| Heat Deflection Temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 59.0 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距6，HDT | ISO 75-2/Af | 66.0 °C | |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 9.5E-5 cm/cm/°C |
| 流动 : -40 到 40°C | ASTM E831 | 9.0E-5 cm/cm/°C | |
| Heat Deflection Temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 201 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/RL-4530 |
|---|---|---|---|
| coefficient of friction | Dynamic | ASTM D3702 | 0.22 |
| tensile strength | 断裂 | ISO 527-2/5 | 55.0 Mpa |
| bending strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 73.0 Mpa |
| Tensile modulus | --1 | ASTM D638 | 2690 Mpa |
| flexural modulus | 50.0 mm 跨距3 | ASTM D790 | 2260 Mpa |
| bending strength | 断裂, 50.0 mm 跨距 | ASTM D790 | 73.0 Mpa |
| elongation | 断裂 | ISO 527-2/5 | 4.7 % |
| Tensile modulus | -- | ISO 527-2/1 | 2960 Mpa |
| elongation | 屈服2 | ASTM D638 | 4.6 % |
| tensile strength | 屈服 | ISO 527-2/5 | 55.0 Mpa |
| 断裂2 | ASTM D638 | 49.0 Mpa | |
| elongation | 断裂2 | ASTM D638 | 4.7 % |
| 屈服 | ISO 527-2/5 | 4.8 % | |
| tensile strength | 屈服2 | ASTM D638 | 52.0 Mpa |
| Wear factor | ASTM D3702 | 2.0E+6 10^-8 mm³/N·m | |
| coefficient of friction | Static | ASTM D3702 | 0.16 |
| flexural modulus | --4 | ISO 178 | 2580 Mpa |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/RL-4530 |
|---|---|---|---|
| Water absorption rate | 24 hr, 50% RH | ASTM D570 | 0.60 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.97 % | |
| shrinkage rate | 横向流动 : 24小时 | ASTM D955 | 1.0 - 3.0 % |
| 流量 : 24小时 | ISO 294-4 | 1.0 - 3.0 % |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/RL-4530 |
|---|---|---|---|
| drying time | 4.0 hr | ||
| screw speed | 30 to 60 rpm | ||
| Suggested maximum moisture content | 0.15 to 0.25 % | ||
| Temperature in the middle of the barrel | 280 to 295 °C | ||
| Temperature at the rear of the barrel | 265 to 275 °C | ||
| Processing (melt) temperature | 275 to 290 °C | ||
| mold temperature | 80 to 95 °C | ||
| drying temperature | 80 °C | ||
| Temperature at the front of the material cylinder | 295 to 305 °C | ||
| Back pressure | 0.200 to 0.300 Mpa |