Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEEK 330G JILIN JOINATURE
ZYPEEK®
Automotive sector、Aerospace
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JILIN JOINATURE/330G |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1U | - kJ/m² | |
| Suspended wall beam without notch impact strength | ISO 180/U | - kJ/m² | |
| Charpy Notched Impact Strength | ISO 179-1eA | 4 kJ/m² | |
| Impact strength of cantilever beam gap | ISO 180/A | 5 kJ/m² |
| Mechanical properties | Test Condition | Test Method | JILIN JOINATURE/330G |
|---|---|---|---|
| Flexural modulus | 23℃ | ISO 178 | 4300 Mpa |
| tensile strength | 屈服，23℃ | ISO 527 | 110 Mpa |
| compressive strength | 23℃ | ISO 604 | 130 Mpa |
| bending strength | 屈服，23℃ | ISO 178 | 175 Mpa |
| Shore hardness | 23℃ | ISO 868 | 85 D 级 |
| Tensile strain | 断裂，23℃ | ISO 527 | 25 % |
| Electrical performance | Test Condition | Test Method | JILIN JOINATURE/330G |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 4 | |
| dielectric strength | 2 mm | IEC 60243-1 | 23 KV/mm |
| dielectric constant | 23 ℃, 1 kHz | IEC 60250 | 3.2 |
| Dissipation Factor | 23℃，1 MHz | IEC 60250 | 0.004 |
| Volume resistivity | 23 ℃，1V | IEC 60093 | 10^16 ohms·cm |
| 275 ℃ | IEC 60093 | 10^9 ohms·cm |
| physical property | Test Condition | Test Method | JILIN JOINATURE/330G |
|---|---|---|---|
| density | 结晶 | ISO 1183 | 1.3 g/cm³ |
| Shrinkage rate | TD | ISO 294-4 | 1 % |
| MD | ISO 294-4 | 1.3 % | |
| Water absorption rate | 23℃，24hr，3.2 mm厚拉伸棒 | ISO 62-1 | 0.07 % |
| melt mass-flow rate | 380℃，5.0kg | ISO 1133 | 80 g/10min |
| Water absorption rate | 平衡，23℃ | ISO 62-1 | 0.4 % |
| density | 非结晶 | ISO 1183 | 1.26 g/cm³ |
| Thermal performance | Test Condition | Test Method | JILIN JOINATURE/330G |
|---|---|---|---|
| Linear coefficient of thermal expansion | 低于Tg沿着流动方向 | ISO 11359 | 50 ppm/K |
| Heat distortion temperature | 1.8 Mpa，HDT | ISO 75-f | 156 °C |
| melting temperature | Tg（起始） | ISO 11357 | 143 °C |
| thermal conductivity | 23℃ | ISO 22007-4 | 0.29 W/m/K |
| Linear coefficient of thermal expansion | 高于Tg沿着流动方向 | ISO 11359 | 120 ppm/K |
| specific heat | 23℃ | DSC | 2.2 kJ/kg /℃ |