Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 TS250G8F5A Grey 浙江新力
--
高流动性,低翘曲,热稳定,尺寸稳定,激光标识
塑壳断路器外壳,机内手柄
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | 浙江新力/TS250G8F5A Grey |
|---|---|---|---|
| Yield bending strength | ISO178 | 260 Mpa | |
| Tensile strength at break | ISO527 | 160 Mpa | |
| Flexural modulus | ISO178 | 10000 Mpa | |
| Charpy Notched Impact Strength | ISO179 | 16 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO179 | 86 kJ/m² | |
| elongation at break | ISO527 | 3.0 % |
| other | Test Condition | Test Method | 浙江新力/TS250G8F5A Grey |
|---|---|---|---|
| Linear forming shrinkage rate | ISO2577 | 0.4 % | |
| Surface Resistivity | IEC60093 | 1.00E+13 Ω | |
| proof tracking index | 3mm | IEC60112 | 250 V |
| Flame retardant performance | Test Condition | Test Method | 浙江新力/TS250G8F5A Grey |
|---|---|---|---|
| Flame retardant performance | 厚度3.0mm | UL94 | ℃ |
| 厚度1.5mm | UL94 | V-2 ℃ | |
| 厚度2.0mm | UL94 | ℃ | |
| 厚度0.8mm | UL94 | ℃ |
| physical property | Test Condition | Test Method | 浙江新力/TS250G8F5A Grey |
|---|---|---|---|
| Water absorption rate | ISO62 | 1.0 % | |
| density | ISO1183 | 1.59 g/cm³ |
| Thermal performance | Test Condition | Test Method | 浙江新力/TS250G8F5A Grey |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa | ISO76 | ℃ |
| GWIT | 厚度3.0mm | IEC60695-2-13 | ℃ |
| GWFI | 厚度3.0mm | IEC60695-2-12 | ℃ |
| GWIT | 厚度1.5mm | IEC60695-2-13 | ℃ |
| 厚度0.8mm | IEC60695-2-13 | ℃ | |
| Heat distortion temperature | 1.8MPa | ISO76 | 200 ℃ |
| GWFI | 厚度0.8mm | IEC60695-2-12 | ℃ |
| GWIT | 厚度2.0mm | IEC60695-2-13 | ℃ |
| GWFI | 厚度2.0mm | IEC60695-2-12 | ℃ |
| 厚度1.5mm | IEC60695-2-12 | 960 ℃ |