PA6 1013NW8 UCHA THAILAND
--
--
Low viscosity、Fast forming cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | UCHA THAILAND/1013NW8 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 5.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | UCHA THAILAND/1013NW8 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3200 Mpa | |
| bending strength | ISO 178 | 110 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 20 % |
| Flexural modulus | ISO 178 | 2700 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 85.0 Mpa |
| Electrical performance | Test Condition | Test Method | UCHA THAILAND/1013NW8 |
|---|---|---|---|
| relative permittivity | IEC 60250 | 3.50 | |
| dielectric strength | IEC 60243-1 | 20 KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| arc resistance | ASTM D495 | 119 sec |
| flammability | Test Condition | Test Method | UCHA THAILAND/1013NW8 |
|---|---|---|---|
| UL flame retardant rating | 0.66mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | UCHA THAILAND/1013NW8 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.2 % |
| TD | 内部方法 | 1.3 % | |
| density | ISO 1183 | 1.14 g/cm³ | |
| Water absorption rate | 平衡,23°C,50%RH | 内部方法 | 2.5 % |
| Thermal performance | Test Condition | Test Method | UCHA THAILAND/1013NW8 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 175 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 65.0 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8E-05 cm/cm/°C |