Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LUX9130T-NAT SABIC INNOVATIVE NANSHA
--
Plastic bag、Lighting applications
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX9130T-NAT
Charpy Notched Impact Strength23°CISO 179/1eA9.0 kJ/m²
Suspended wall beam without notch impact strength-30°C7ISO 180/1U130 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength-30°CASTM D4812无断裂
Charpy Notched Impact Strength-30°CISO 179/1eA9.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength23°C7ISO 180/1U130 kJ/m²
Dart impact23°C, Total EnergyASTM D376355.0 J
Suspended wall beam without notch impact strength23°CASTM D4812无断裂
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX9130T-NAT
Tensile modulus--2ASTM D6382370 Mpa
tensile strength 屈服3ASTM D63864.0 Mpa
elongation断裂3ASTM D63872 %
断裂ISO 527-2/5052 %
Flexural modulus--5ISO 1782410 Mpa
50.0 mm 跨距4ASTM D7902300 Mpa
tensile strength 断裂ISO 527-2/5050.0 Mpa
屈服ISO 527-2/5064.0 Mpa
elongation屈服ISO 527-2/506.0 %
屈服3ASTM D6386.0 %
bending strength屈服, 50.0 mm 跨距ASTM D79098.0 Mpa
tensile strength 断裂3ASTM D63859.0 Mpa
Tensile modulus--ISO 527-2/12400 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX9130T-NAT
Dissipation Factor1.10 GHzASTM ES7-835.8E-3
dielectric constant1.10 GHzASTM ES7-832.81
Compared to the Leakage Tracking Index (CTI)UL 746PLC 2
optical performance Test ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX9130T-NAT
transmissivity3000 µm内部方法> 89.5 %
6000 µmASTM D1003> 88.0 %
1000 µm内部方法> 90.5 %
2000 µm内部方法> 90.0 %
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX9130T-NAT
UL flame retardant rating6.0 mmUL 945VA
Hot filament ignition temperature1.5 mmIEC 60695-2-13850 °C
UL flame retardant rating0.40 mmUL 94V-2
1.5 mmUL 94V-0
Burning wire flammability index1.5 mmIEC 60695-2-12960 °C
physical property Test ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX9130T-NAT
Water absorption rate平衡, 23°C, 50% RHISO 620.010 %
Shrinkage rate横向流动 : 3.20 mm内部方法0.50 - 0.70 %
Melt volume flow rate300°C/1.2 kgISO 113317.0 cm3/10min
melt mass-flow rate300°C/1.2 kgASTM D123818 g/10 min
Shrinkage rate流动 : 3.20 mm内部方法0.45 - 0.65 %
Water absorption rate饱和, 23°CISO 620.10 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX9130T-NAT
Linear coefficient of thermal expansion流动 : -40 到 40°CASTM E8317.1E-5 cm/cm/°C
vicat--ASTM D15259137 °C
Linear coefficient of thermal expansion横向 : 23 到 80°CISO 11359-28.0E-5 cm/cm/°C
Heat distortion temperature0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距8，HDTISO 75-2/Be131 °C
Linear coefficient of thermal expansion流动 : 23 到 80°CISO 11359-27.4E-5 cm/cm/°C
Heat distortion temperature0.45 MPa, 未退火, 3.20 mm，HDTASTM D648131 °C
ball-indentation hardness123 到 127°CIEC 60695-10-2通过
Heat distortion temperature1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距8，HDTISO 75-2/Ae120 °C
vicat--ISO 306/B120139 °C
RTI ImpUL 746115 °C
Linear coefficient of thermal expansion横向 : -40 到 40°CASTM E8317.1E-5 cm/cm/°C
Heat distortion temperature1.8 MPa, 未退火, 3.20 mm，HDTASTM D648120 °C
RTI ElecUL 746115 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX9130T-NAT
screw speed40 to 70 rpm
Suggested maximum moisture content0.020 %
Processing (melt) temperature290 to 310 °C
drying temperature120 °C
Suggested injection volume40 to 60 %
drying time3.0 to 4.0 hr
Temperature in the middle of the barrel275 to 300 °C
Temperature at the rear of the barrel265 to 290 °C
Exhaust hole depth0.025 to 0.076 mm
Temperature at the front of the material cylinder290 to 310 °C
Back pressure0.300 to 0.700 Mpa
Temperature70 to 95 °C
Spray nozzle temperature280 to 305 °C