LDPE F2200 ASIA POLYMER TAIWAN
POLYMER-E
film,Pipe fittings
High transparency
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | ASIA POLYMER TAIWAN/F2200 | |
|---|---|---|---|
| melt mass-flow rate | ASTM D-1238 | 2.3 g/10min |
| Basic performance | Test Condition | Test Method | ASIA POLYMER TAIWAN/F2200 |
|---|---|---|---|
| density | ASTM D-1505 | 0.922 g/cm³ |
| Mechanical properties | Test Condition | Test Method | ASIA POLYMER TAIWAN/F2200 |
|---|---|---|---|
| elongation | 纵向 | ASTM D-882 | 320 % |
| coefficient of friction | ASTM D-1894 | <0.77 | |
| Shore hardness | D | ASTM D-2240 | 52 |
| elongation | 横向 | ASTM D-882 | 540 % |
| tear strength | 纵向 | ASTM D-1922 | 110 kg/cm |
| Flexural modulus | 纵向，1%伸长率, 薄膜 | ASTM D-882 | 1970 kg/cm2 |
| tensile strength | 横向，断裂 | ASTM D-882 | 160 kg/cm2 |
| 纵向，断裂 | ASTM D-882 | 250 kg/cm2 | |
| Flexural modulus | 横向，1%伸长率, 薄膜 | ASTM D-882 | 2250 kg/cm2 |
| Impact strength of cantilever beam gap | ASTM D-1709 | 90 g.50%F | |
| tear strength | 横向 | ASTM D-1922 | 72 kg/cm |
| optical performance | Test Condition | Test Method | ASIA POLYMER TAIWAN/F2200 |
|---|---|---|---|
| turbidity | ASTM D-1003 | 4.6 % | |
| gloss | 60度角 | ASTM D-2457 | 120 % |
| Thermal performance | Test Condition | Test Method | ASIA POLYMER TAIWAN/F2200 |
|---|---|---|---|
| Low temperature brittleness temperature | ASTM D-746 | <-70 °C | |
| vicat | ASTM D-1525 | 96 °C | |
| Heat distortion temperature | 66psi，HDT | ASTM D-648 | 48 °C |