PC ML-3107ZLP TEIJIN SHANGHAI
PANLITE®
Household appliances、Electronic field、Electrical field
optical performance 、High temperature resistan、UV resistance、Flame retardant、transparent、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | TEIJIN SHANGHAI/ML-3107ZLP |
|---|---|---|---|
| Tensile strength at break | 50mm/min | ISO 527-1 | 68 Mpa |
| elongation at break | 50mm/min | ISO 527-1 | 105 % |
| Yield tensile strength | 50mm/min | ISO 527-1,2 | 61 Mpa |
| Notch impact strength | Notched | ISO 179 | 15 kJ/m² |
| bending strength | 2mm/min | ISO 178 | 99 Mpa |
| Flexural modulus | 2mm/min | ISO 178 | 2400 Mpa |
| optical performance | Test Condition | Test Method | TEIJIN SHANGHAI/ML-3107ZLP |
|---|---|---|---|
| transmittance | 1.5mmt | JIS K7136 | 61 % |
| dispersity | 2.0mmt | In-house method | 57 % |
| physical property | Test Condition | Test Method | TEIJIN SHANGHAI/ML-3107ZLP |
|---|---|---|---|
| Dissolving fingers | 300℃ | ISO 1133 | 18 cm310min |
| Shrinkage rate | MD | In-house method | 0.5-0.7 % |
| TD | In-house method | 0.5-0.7 % |
| Thermal performance | Test Condition | Test Method | TEIJIN SHANGHAI/ML-3107ZLP |
|---|---|---|---|
| 线膨胀系数，MD | ISO 11359-2 | 0.7 X10-4/℃ | |
| TD | ISO 11359-2 | 0.7 X10-4/℃ | |
| 1.80MPa | ISO 75-1,2 | 129 °C | |
| Flame retardancy | 1.0mm/3.0mm | UL94 | V-2 |