Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 5010N6 BK MITSUBISHI ENGINEERING JAPAN
NOVADURAN™
Bottle cap,Automotive Applications
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010N6 BK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 120 kJ/m² |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010N6 BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2800 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 55.0 Mpa |
| bending strength | ISO 178 | 90.0 Mpa | |
| Flexural modulus | ISO 178 | 2600 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 50 % |
| 屈服 | ISO 527-2/50 | 4.3 % |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010N6 BK |
|---|---|---|---|
| dielectric strength | 2.00 mm | IEC 60243-1 | 18 KV/mm |
| Dissipation Factor | 1 MHz | IEC 60250 | 0.020 |
| Volume resistivity | IEC 60093 | 1.0E+16 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 1 | |
| Surface Resistivity | IEC 60093 | 1.0E+15 ohms | |
| dielectric strength | 1.00 mm | IEC 60243-1 | 21 KV/mm |
| dielectric constant | 1 MHz | IEC 60250 | 3.20 |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010N6 BK |
|---|---|---|---|
| UL flame retardant rating | 0.71 mm | UL 94 | V-0 |
| 3.2 mm | UL 94 | V-0 | |
| 1.6 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010N6 BK |
|---|---|---|---|
| Shrinkage rate | 横向流量 : 2.00 mm | 内部方法 | 1.8 % |
| 流量 : 2.00 mm | 内部方法 | 1.9 % | |
| Melt volume flow rate | 250°C/2.16 kg | ISO 1133 | 20.0 cm3/10min |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.080 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010N6 BK |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 224 °C | |
| Linear coefficient of thermal expansion | 流动 : -30 到 35°C | ISO 11359-2 | 8.0E-5 cm/cm/°C |
| 横向 : 35 到 120°C | ISO 11359-2 | 1.5E-4 cm/cm/°C | |
| Heat distortion temperature | 0.45 MPa, 退火，HDT | ISO 75-2/B | 165 °C |
| Linear coefficient of thermal expansion | 流动 : 35 到 120°C | ISO 11359-2 | 1.4E-4 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 退火，HDT | ISO 75-2/A | 77.0 °C |
| RTI Elec | 0.71 mm | UL 746 | 140 °C |
| Linear coefficient of thermal expansion | 横向 : -30 到 120°C | ISO 11359-2 | 1.2E-4 cm/cm/°C |
| RTI Imp | 0.71 mm | UL 746 | 120 °C |
| Linear coefficient of thermal expansion | 横向 : -30 到 35°C | ISO 11359-2 | 8.8E-5 cm/cm/°C |
| RTI | 0.71 mm | UL 746 | 140 °C |
| Linear coefficient of thermal expansion | 流动 : -30 到 120°C | ISO 11359-2 | 1.2E-4 cm/cm/°C |
| injection | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010N6 BK |
|---|---|---|---|
| screw speed | 80 to 120 rpm | ||
| Temperature in the middle of the barrel | 240 °C | ||
| Temperature at the rear of the barrel | 235 °C | ||
| Injection Pressure | 20.0 to 150 Mpa | ||
| Drying Temperature - Vacuum Drying Machine | 120 °C | ||
| Temperature at the front of the material cylinder | 250 °C | ||
| Drying time - vacuum dryer | 5.0 to 8.0 hr | ||
| Temperature | 60 to 80 °C | ||
| injection speed | 中等偏快 | ||
| Spray nozzle temperature | 245 °C |