Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPU 1185A10 BASF SHANGHAI
Elastollan®
Bottle cap,Automotive Applications,Fitness equipment,Cable
transparent,wear resistant,Low temperature resistanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | BASF SHANGHAI/1185A10 |
|---|---|---|---|
| Shore hardness | 邵氏A | ASTM D2240 | 85 |
| Mechanical properties | Test Condition | Test Method | BASF SHANGHAI/1185A10 |
|---|---|---|---|
| Taber abraser | ASTM D1044 | 30.0 mg | |
| wear resistance | DIN 53516 | 25 mm³ | |
| Tensile modulus | 注塑 | ASTM D412 | 20.7 Mpa |
| Flexural modulus | 注塑 | ASTM D790 | 29.0 Mpa |
| flammability | Test Condition | Test Method | BASF SHANGHAI/1185A10 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | BASF SHANGHAI/1185A10 |
|---|---|---|---|
| melt mass-flow rate | 190°C/21.6kg | ASTM D1238 | 1.0to20 g/10min |
| 190°C/8.7kg | ASTM D1238 | 1.0to10 g/10min |
| elastomer | Test Condition | Test Method | BASF SHANGHAI/1185A10 |
|---|---|---|---|
| tensile strength | 100%应变 | ASTM D412 | 9.65 Mpa |
| elongation | 断裂 | ASTM D412 | 530 % |
| compression set | 70°C,22hr | ASTM D395B | 45 % |
| tensile strength | ASTM D412 | 35.9 Mpa | |
| 300%应变 | ASTM D412 | 21.4 Mpa | |
| compression set | 23°C,22hr | ASTM D395B | 25 % |
| tear strength | ASTM D624 | 110 kN/m |
| Thermal performance | Test Condition | Test Method | BASF SHANGHAI/1185A10 |
|---|---|---|---|
| vicat | ASTM D1525 | 100 °C | |
| 内部方法 | 66 °C | ||
| Glass Transition Temperature | 内部方法 | -38.0 °C |