Product Name / Manufacturer / Model

Brand

Typical Applications

Properties

Color

Form

Processing Methods

Grade

Filler

Recycled Content

Certificates

Reference Price

PEI
PEI SABIC INNOVATIVE US 1000P-1000
Injection grade
US$ 10,250 / MT
FOB Guangzhou port, China
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/1000P-1000
bending strengthISO 178160 Mpa
Bending modulusISO 1783300 Mpa
Tensile strainYieldISO 527-2/506.0 %
Taber abraser1000 Cycles, 1000 g, CS-17 WheelInternal Method10.0 mg
Tensile modulusISO 527-2/13200 Mpa
tensile strengthBreakISO 527-2/5085.0 Mpa
YieldISO 527-2/50105 Mpa
Tensile strainBreakISO 527-2/5060 %
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/1000P-1000
Linear coefficient of thermal expansionAcross Flow : 23 to 150°CISO 11359-25.0E-5 cm/cm/°C
Flow : 23 to 150°CISO 11359-25.0E-5 cm/cm/°C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 100 mm SpanISO 75-2/Ae190 °C
Vicat softening temperature--ISO 306/B50211 °C
RTI ElecUL 746170 °C
RTI ImpUL 746170 °C
Vicat softening temperature--ISO 306/A50215 °C
RTIUL 746170 °C
thermal conductivityISO 83020.24 W/m/K
Hot deformation temperature0.45 MPa, Unannealed, 4.00 mm, 100 mm SpanISO 75-2/Be200 °C
Vicat softening temperature--ISO 306/B120212 °C
Ball Pressure Test123 to 127°CIEC 60695-10-2通过
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/1000P-1000
UL flame retardant rating0.40 mmUL 94V-2
Extreme Oxygen IndexISO 4589-247 %
UL flame retardant rating3.0 mmUL 945VA
0.75 mmUL 94V-0
Burning wire flammability index3.2 mmIEC 60695-2-12960 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE US/1000P-1000
Temperature at the front of the material cylinder360 to 415 °C
Mold temperature140 to 180 °C
Processing (melt) temperature370 to 410 °C
Suggested maximum moisture content0.020 %
Spray nozzle temperature350 to 405 °C
drying temperature150 °C
Temperature in the middle of the barrel350 to 405 °C
drying time4.0 to 6.0 hr
Hopper temperature80 to 120 °C
Temperature at the rear of the barrel340 to 395 °C
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/1000P-1000
Dielectric strength0.800 mm, in OilIEC 60243-133 KV/mm
Compared to the anti leakage trace indexSolution BIEC 60112PLC 4
Volume resistivityIEC 600931.0E+15 ohms·cm
Dielectric strength3.20 mm, in OilIEC 60243-116 KV/mm
Dissipation factor2.45 GHzIEC 602502.5E-3
Relative permittivity1 MHzIEC 602502.90
Surface resistivityIEC 60093> 1.0E+15 ohms
Dielectric strength1.60 mm, in OilIEC 60243-125 KV/mm
Dissipation factor50 HzIEC 602505.0E-4
Relative permittivity60 HzIEC 602502.90
Dissipation factor60 HzIEC 602505.0E-4
1 MHzIEC 602506.0E-3
Relative permittivity50 HzIEC 602502.90
Compared to the anti leakage trace index--IEC 60112PLC 4
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/1000P-1000
Water absorption rateSaturation, 23°CISO 621.3 %
Melt Volume Flow Rate (MVR)360°C/5.0 kgISO 113313.0 cm3/10min
Shrinkage rateFlowInternal Method0.50 - 0.70 %
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.70 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE US/1000P-1000
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Impact strength of cantilever beam gap23°CISO 180/1A6.0 kJ/m²
-30°CISO 180/1A6.0 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
hardnessTest ConditionTest MethodSABIC INNOVATIVE US/1000P-1000
Ball Pressure TestH 358/30ISO 2039-1140 Mpa

Supplier Join

Contact Us

Get App

Top

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index

+86 0755 27873515

Room 906, Global Digital Building, No. 9 Gaoxin Middle 3rd Road, Maling Community, Yuehai Subdistrict, Nanshan District, Shenzhen, Guangdong Province, China