Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 UNITIKA Nylon 6 A1022GFL15 UNITIKA JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | UNITIKA JAPAN/UNITIKA Nylon 6 A1022GFL15 |
|---|---|---|---|
| Charpy Notched Impact Strength | kJ/m² | 7.0 14 | |
| Impact strength of simply supported beam without notch | kJ/m² | 23 33 |
| hardness | Test Condition | Test Method | UNITIKA JAPAN/UNITIKA Nylon 6 A1022GFL15 |
|---|---|---|---|
| Rockwell hardness | R计秤 | 116 103 |
| Electrical performance | Test Condition | Test Method | UNITIKA JAPAN/UNITIKA Nylon 6 A1022GFL15 |
|---|---|---|---|
| Volume resistivity | ohms·cm | 2E+15 8E+13 | |
| dielectric strength | 1.00mm | kV/mm | 39 36 |
| dielectric constant | 1MHz | 3.30 -- |
| Mechanical properties | Test Condition | Test Method | UNITIKA JAPAN/UNITIKA Nylon 6 A1022GFL15 |
|---|---|---|---|
| bending strength | MPa | 175 100 | |
| Flexural modulus | MPa | 5000 2800 | |
| tensile strength | 断裂 | MPa | 120 70.0 |
| Tensile strain | 断裂 | % | 2.7 4.6 |
| Tensile modulus | MPa | 5600 3000 |
| flammability | Test Condition | Test Method | UNITIKA JAPAN/UNITIKA Nylon 6 A1022GFL15 |
|---|---|---|---|
| UL flame retardant rating | 0.9mm | HB HB |
| physical property | Test Condition | Test Method | UNITIKA JAPAN/UNITIKA Nylon 6 A1022GFL15 |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | % | 0.80to1.0 0.80到1.0 |
| MD:3.20mm | % | 0.30to0.50 0.30到0.50 | |
| Water absorption rate | 23°C,24hr | % | 1.5 1.5 |
| 平衡,23°C,50%RH | % | 2.4 2.4 | |
| density | g/cm³ | 1.23 1.23 |
| Thermal performance | Test Condition | Test Method | UNITIKA JAPAN/UNITIKA Nylon 6 A1022GFL15 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 214 -- |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 4.2E-05 4.2E-05 |
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 190 -- |