Melt mass flow rate

337°C/6.6 kg

ASTM D1238

g/10 min

1

Shrinkage rate - flow

3.20 mm

内部方法

%

0

Water absorption rate

24 hr

ASTM D570

%

0

Water absorption rate

平衡, 23°C

ASTM D570

%

1

Reverse notch impact

3.20 mm

ASTM D256

J/m

1

Tensile modulus

ASTM D638

Mpa

3

tensile strength

屈服

ASTM D638

Mpa

1

Falling hammer impact

23°C

ASTM D3029

J

3

Elongation rate

屈服

ASTM D638

%

7

Elongation rate

断裂

ASTM D638

%

6

Taber abraser

1000 Cycles, 1000 g, CS-17 转轮

ASTM D1044

mg

1

Bending modulus

100 mm 跨距

ASTM D790

Mpa

3

bending strength

屈服, 100 mm 跨距

ASTM D790

Mpa

1

Non notched cantilever beam impact

23°C

ASTM D4812

J/m

1

RTI

UL 746

°C

1

RTI Elec

UL 746

°C

1

RTI Imp

UL 746

°C

1

thermal conductivity

ASTM C177

W/m/K

0

Hot deformation temperature

0.45 MPa, 未退火, 6.40 mm

ASTM D648

°C

2

Hot deformation temperature

1.8 MPa, 未退火, 6.40 mm

ASTM D648

°C

1

vicat softening point

ASTM D15255

°C

2

Linear coefficient of thermal expansion - flow

-20 到 150°C

ASTM E831

cm/cm/°C

5

Dielectric strength

1.60 mm, in Air

ASTM D149

KV/mm

3

Dielectric strength

1.60 mm, in Oil

ASTM D149

KV/mm

2

Volume resistivity

ASTM D257

ohms·cm

1

Extreme Oxygen Index

ASTM D2863

%

4