Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM KX09024 SABIC INNOVATIVE US
LNP™ FARADEX™
Automotive Applications
heat-resisting,high strength,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/KX09024 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 9.0 kJ/m² |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/KX09024 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:23到60°C | ISO 11359-2 | 1.6E-04 cm/cm/°C |
| MD:23到60°C | ISO 11359-2 | 1.4E-04 cm/cm/°C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 67.0 °C | |
| 0.45MPa, Unanealed, 64.0mm span | ISO 75-2/Bf | 136 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/KX09024 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 1000 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 12 % |
| bending strength | ISO 178 | 48.0 Mpa | |
| flexural modulus | ISO 178 | 1400 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/KX09024 |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1.0E+8-1.0E+10 ohms | |
| volume resistivity | ASTM D257 | 1.0E+8-1.0E+10 ohms·cm |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/KX09024 |
|---|---|---|---|
| shrinkage rate | MD | 内部方法 | 2.8 % |