Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 B 30GF VOA POLIBLEND ITALY
POLIMID B
--
Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLIBLEND ITALY/B 30GF VOA |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ISO 180 | 48 kJ/m² |
| Electrical performance | Test Condition | Test Method | POLIBLEND ITALY/B 30GF VOA |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 |
| Mechanical properties | Test Condition | Test Method | POLIBLEND ITALY/B 30GF VOA |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 9200 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.5 % |
| 屈服 | ISO 527-2 | 2.5 % | |
| tensile strength | 断裂 | ISO 527-2 | 130 Mpa |
| 屈服 | ISO 527-2 | 130 Mpa |
| flammability | Test Condition | Test Method | POLIBLEND ITALY/B 30GF VOA |
|---|---|---|---|
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 775 °C |
| UL flame retardant rating | 3.2mm | UL 94 | V-0 |
| 0.8mm | UL 94 | V-0 | |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | POLIBLEND ITALY/B 30GF VOA |
|---|---|---|---|
| Shrinkage rate | 0.40-0.60 % | ||
| Water absorption rate | 23°C,24hr | ISO 62 | 1.0 % |
| Thermal performance | Test Condition | Test Method | POLIBLEND ITALY/B 30GF VOA |
|---|---|---|---|
| Heat distortion temperature | 连续使用温度3，HDT | 100 °C | |
| vicat | ISO 306/A120 | 220 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 205 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 200 °C | |
| ball-indentation hardness | 165°C | IEC 60695-10-2 | 通过 |
| melting temperature | DSC | 222 °C |