PBT CN7030NN JAPAN POLYPLASTIC
DURANEX®
Automotive sector
Glass fiber reinforced、Flame retardant、Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JAPAN POLYPLASTIC/CN7030NN |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/CN7030NN |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 95 |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/CN7030NN |
|---|---|---|---|
| bending strength | ISO 178 | 200 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.9 % |
| Flexural modulus | ISO 178 | 10300 Mpa | |
| tensile strength | ISO 527-2 | 127 Mpa |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/CN7030NN |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 20 KV/mm |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/CN7030NN |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/CN7030NN |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.10 % |
| density | ISO 1183 | 1.69 g/cm³ |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/CN7030NN |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 7E-05 cm/cm/°C |
| MD：23到55°C | 内部方法 | 2E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 208 °C |