ABS 884 X01 TORAY JAPAN
Toyolac® 
Industrial machinery、Fitness equipment
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodTORAY JAPAN/884 X01
Rockwell hardnessR级ASTM D785104
Mechanical propertiesTest ConditionTest MethodTORAY JAPAN/884 X01
bending strengthASTM D790/ISO 178693 kg/cm²(MPa)[Lb/in²]
Tensile modulusISO 527-2/12700 Mpa
Flexural modulusASTM D790/ISO 17823550 kg/cm²(MPa)[Lb/in²]
bending strengthASTM D79068.0 Mpa
elongation at breakASTM D638/ISO 5275 %
tensile strength ASTM D638/ISO 527459 kg/cm²(MPa)[Lb/in²]
Flexural modulusASTM D7902310 Mpa
tensile strength 屈服ISO 527-2/5049.0 Mpa
elongation断裂ASTM D638>5.0 %
bending strengthISO 17870.0 Mpa
Tensile modulusASTM D638/ISO 52727557 kg/cm²(MPa)[Lb/in²]
tensile strength 屈服ASTM D63845.0 Mpa
Tensile strain断裂ISO 527-2/50>5.0 %
otherTest ConditionTest MethodTORAY JAPAN/884 X01
characteristic阻燃性能
purpose汽车配件
Physical propertiesTest ConditionTest MethodTORAY JAPAN/884 X01
Shrinkage rateASTM D9550.004-0.007 %
densityASTM D792/ISO 11831.15
melt mass-flow rateASTM D1238/ISO 11335 g/10min
flammabilityTest ConditionTest MethodTORAY JAPAN/884 X01
UL flame retardant rating0.75mmUL 94V-2
2.5mmUL 945VA
1.5mmUL 94V-0
physical property Test ConditionTest MethodTORAY JAPAN/884 X01
Shrinkage rateMDASTM D9550.40-0.70 %
melt mass-flow rate200°C/5.0kgISO 11335.0 g/10min
Thermal performanceTest ConditionTest MethodTORAY JAPAN/884 X01
Heat distortion temperature1.8MPa,未退火,6.40mm，HDTASTM D64876.0 °C
1.8MPa,未退火，HDTISO 75-2/A70.0 °C