Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM 500AL NC010 DUPONT SHENZHEN
Delrin®
Household appliances、Industrial applications、Automotive sector、Electronic field、Electrical field、Non specific food applica
Dimensional stability、Fatigue resistance、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT SHENZHEN/500AL NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 160 kJ/m² |
| -30°C | ISO 179/1eU | 130 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT SHENZHEN/500AL NC010 |
|---|---|---|---|
| Emission | VDA275 | <8.00 mg/kg |
| Mechanical properties | Test Condition | Test Method | DUPONT SHENZHEN/500AL NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3000 Mpa | |
| Tensile creep modulus | 1hr | ISO 899-1 | 2400 Mpa |
| Nominal tensile fracture strain | ISO 527-2 | 23 % | |
| Flexural modulus | ISO 178 | 2800 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 11 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1600 Mpa |
| tensile strength | 屈服 | ISO 527-2 | 66.0 Mpa |
| flammability | Test Condition | Test Method | DUPONT SHENZHEN/500AL NC010 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 0.75mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| burning rate | 1.00mm | ISO 3795 | 28 mm/min |
| physical property | Test Condition | Test Method | DUPONT SHENZHEN/500AL NC010 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 12.0 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.7 % |
| MD | ISO 294-4 | 1.8 % | |
| melt mass-flow rate | ISO 1133 | 14 g/10min | |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.30 % |
| Thermal performance | Test Condition | Test Method | DUPONT SHENZHEN/500AL NC010 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 178 °C | |
| AnnealingTemperature | 160 °C | ||
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 164 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 97.0 °C | |
| AnnealingTime-Optional | 30.0 min/mm | ||
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| TD | ISO 11359-2 | 1.2E-04 cm/cm/°C |