Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM MT8F02 CELANESE GERMANY
HOSTAFORM®
Fitness equipment,Automotive Applications,Thin walled products
heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE GERMANY/MT8F02 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.0 kJ/m² |
| -30°C | ISO 179/1eA | 4.0 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 60 kJ/m² |
| -30°C | ISO 179/1eU | 60 kJ/m² |
| Mechanical properties | Test Condition | Test Method | CELANESE GERMANY/MT8F02 |
|---|---|---|---|
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 7.0 % |
| Tensile creep modulus | 1hr | ISO 899-1 | 2100 Mpa |
| Tensile modulus | ISO 527-2/1A/1 | 2500 Mpa | |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1200 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2400 Mpa |
| Nominal tensile fracture strain | ISO 527-2/1A/50 | 16 % | |
| tensile strength | 屈服 | ISO 527-2/1A/50 | 48.0 Mpa |
| physical property | Test Condition | Test Method | CELANESE GERMANY/MT8F02 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 6.00 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.7 % |
| MD | ISO 294-4 | 2.0 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.20 % |
| density | ISO 1183 | 1.52 g/cm³ |
| Thermal performance | Test Condition | Test Method | CELANESE GERMANY/MT8F02 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 166 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 98.0 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.1E-04 cm/cm/°C |